ExxonMobil LDPE LD 100BW Low Density Polyethylene Resin (European Grade)

Category	Polymer , Thermoplastic , Polyethylene (PE) , LDPE
Manufacturer	Exxon Chemical
Trade Name	LDPE
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	ExxonMobil LDPE LD 100BW Low Density Polyethylene Resin (European Grade).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Product Description: LD 100BW is a LDPE containing low antioxidants suitable for the production of LV and MV crosslinked insulation using the 1-step or 2-step silane technology. Through in-house compounding it can be used in Medium Voltage peroxide cross-linkable insulation. Sufficient antioxidant and Cu-inhibitor should be added to meet specific ageing requirements.Availability: Europe Additive: Thermal Stabilizer: YesApplications: LV silane cross-linkable insulation- 2-step processMV/HV peroxide cross-linked insulationInformation provided by ExxonMobil

Physical Properties	Metric	English	Comments
Density	0.923 g/cc	0.0333 lb/in³	ExxonMobil method
Melt Flow	2.0 g/10 min @Load 2.16 kg, Temperature 190 °C	2.0 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Hardness, Shore D	49 @Time 15.0 sec	49 @Time 0.00417 hour	ASMT D2240
Tensile Strength at Break	11.7 MPa	1700 psi	ASTM D638
Tensile Strength, Yield	11.0 MPa	1600 psi	ASTM D638
Elongation at Break	610 %	610 %	ASTM D638
Elongation at Yield	20 %	20 %	ASTM D638
Flexural Modulus, 1% Secant	221 MPa	32000 psi	ASTM D790

Thermal Properties	Metric	English	Comments
Melting Point	<= 230 °C	<= 446 °F	Peak Melting Point; ExxonMobil method

Electrical Properties	Metric	English	Comments
Volume Resistivity	7.00e+15 ohm-cm	7.00e+15 ohm-cm	ASTM D257
Dielectric Constant	2.2	2.2	STM D150
Dielectric Strength	55.1 kV/mm	1400 kV/in	ASTM D149
Dissipation Factor	0.00050	0.00050	STM D150