- Lehmann & Voss LUVOCOM® 1105/GF/40 PEEK, with glass fiber
Lehmann & Voss LUVOCOM® 1105/GF/40 PEEK, with glass fiber
| Category | Polymer , Thermoplastic , Polyketone , Polyetheretherketone (PEEK) , Polyetheretherketone, PEEK, Glass Fiber Filled |
| Manufacturer | Lehmann & Voss & Co. |
| Trade Name | LUVOCOM® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lehmann & Voss LUVOCOM® 1105/GF/40 PEEK, with glass fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.Strong, stiff parts; impact resistance.Dynamic stressed parts at high movement velocity.Chemical and hydrolysis resistance parts, non flammable.High dimensionally stable precision parts, high continuous use temperature.Bearings, sleeves, control disks, gear wheels, pump impellers, gear parts.Information provided by Lehmann & Voss & Co.KG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.62 g/cc | 1.62 g/cc | ISO 1183 |
| Water Absorption | <= 0.10 % | <= 0.10 % | 23°C/24h |
| Linear Mold Shrinkage | 0.0020 - 0.0050 cm/cm | 0.0020 - 0.0050 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Stress | 200 MPa | 29000 psi | |
| Elongation at Yield | 2.5 % | 2.5 % | |
| 3.0 % | 3.0 % | flexural | |
| Modulus of Elasticity | 14.0 GPa | 2030 ksi | |
| Flexural Strength | 260 MPa | 37700 psi | |
| Flexural Modulus | 12.0 GPa | 1740 ksi | |
| Charpy Impact Unnotched | 3.00 J/cm² | 14.3 ft-lb/in² | flatwise; ISO 179 1fU |
| 2.50 J/cm² @Temperature -30.0 °C |
11.9 ft-lb/in² @Temperature -22.0 °F |
ISO 179 | |
| Coefficient of Friction, Dynamic | 0.31 | 0.31 | |
| Coefficient of Friction, Static | 0.29 | 0.29 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 18.0 µm/m-°C | 10.0 µin/in-°F | DIN 53752 |
| Thermal Conductivity | 0.420 W/m-K | 2.91 BTU-in/hr-ft²-°F | DIN 52612 |
| Maximum Service Temperature, Air | 250 °C | 482 °F | |
| 280 °C | 536 °F | short term | |
| Vicat Softening Point | 325 °C | 617 °F | DIN ISO 306 |
| Flammability, UL94 | V-0 | V-0 | not recognized by UL |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Insulation Resistance | >= 1.00e+12 ohm | >= 1.00e+12 ohm |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 390 °C | 734 °F | mass temp |
| Nozzle Temperature | 360 - 380 °C | 680 - 716 °F | |
| Zone 1 | 360 - 370 °C | 680 - 698 °F | |
| Zone 2 | 380 - 390 °C | 716 - 734 °F | |
| Zone 3 | 390 - 400 °C | 734 - 752 °F | |
| Mold Temperature | 170 - 200 °C | 338 - 392 °F | |
| Drying Temperature | 120 °C @Time 21600 - 28800 sec |
248 °F @Time 6.00 - 8.00 hour |
or |
| 150 °C @Time 10800 - 21600 sec |
302 °F @Time 3.00 - 6.00 hour |
Dehumidifying dryer |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | natural color |
Users viewing this material also viewed the following:
- Oxford Polymers 10GF 10% Glass Fiber Filled Polycarbonate for Injection Molding
- SABIC Innovative Plastics Cycoloy® XCM850 PC+ABS (Asia Pacific)
- Nabaltec ACTILOX® 200SM AlO(OH) Boehmite
- LG Chemical LUMAX IN-5001 High Impact PBT
- Hexcel® HexPly® 954-6 Curing Cyanate Resin, M40J Fiber
- Eagle Brass 725 Copper Nickel Tin, Extra Spring
- Covestro Makrofol® ID 6-2 laserable Polycarbonate
- Arkema Group OREVAC® 18510 Grafted Maleic Anhydride Polyethylene
- Chevron Phillips Ryton® PR09 Polyphenylene Sulfide Resin (discontinued **)
- Lehmann & Voss LUVOCOM® 1105-7825 PEEK, with PTFE
Copyright © lookpolymers.com All Rights Reserved