Multibase TPSiV® 3111-70A Thermoplastic Elastomer

Category	Polymer , Thermoplastic , Elastomer, TPE , Thermoplastic Vulcanizate Elastomer (TPV) , Silicone, Thermoplastic
Manufacturer	Multibase
Trade Name	TPSiV®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Multibase TPSiV® 3111-70A Thermoplastic Elastomer.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

TPSiV™ material for injection molding and extrusion applicationsAPPLICATIONS: Solution for appliance, sports and leisure, and construction applications where excellent hydrolysis resistance, high and/or low temperature resistance, and abrasion resistance are required.; NFS and FDA Compliance.FEATURES and BENEFITS: This TPSiV™ material has the following features and benefits: Smooth, silky feel; Excellent hydrolysis resistance; Excellent high temperature performance in air; Excellent low temperature flexibility; Excellent abrasion resistance; Bonds without adhesives to PC, ABS, PU, and PVC; Plastizer freeCOMPOSITION: Vulcanized silicone thermoplastic resinInformation provided by Multibase, a Dow Corning Company

Physical Properties	Metric	English	Comments
Specific Gravity	1.15 g/cc	1.15 g/cc	ASTM D792

Mechanical Properties	Metric	English	Comments
Hardness, Shore A	70	70	ASTM D2240
	60 @Treatment Temp. 140 °C, Time 3.629e+6 sec	60 @Treatment Temp. 284 °F, Time 1008 hour	heat aging; ASTM D573-99
	67 @Treatment Temp. 120 °C, Time 3.629e+6 sec	67 @Treatment Temp. 248 °F, Time 1008 hour	heat aging; ASTM D573-99
	75 @Treatment Temp. 100 °C, Time 3.60e+6 sec	75 @Treatment Temp. 212 °F, Time 1000 hour	water immersion
Tensile Strength	15.0 MPa	2180 psi	ASTM D412
	8.85 MPa @Treatment Temp. 140 °C, Time 3.629e+6 sec	1280 psi @Treatment Temp. 284 °F, Time 1008 hour	heat aging; ASTM D573-99
	11.25 MPa @Treatment Temp. 100 °C, Time 3.60e+6 sec	1632 psi @Treatment Temp. 212 °F, Time 1000 hour	water immersion
	12.15 MPa @Treatment Temp. 120 °C, Time 3.629e+6 sec	1762 psi @Treatment Temp. 248 °F, Time 1008 hour	heat aging; ASTM D573-99
Elongation at Break	600 %	600 %	ASTM D412
	378 % @Treatment Temp. 140 °C, Time 3.629e+6 sec	378 % @Treatment Temp. 284 °F, Time 1008 hour	heat aging; ASTM D573-99
	480 % @Treatment Temp. 100 °C, Time 3.60e+6 sec	480 % @Treatment Temp. 212 °F, Time 1000 hour	water immersion
	702 % @Treatment Temp. 120 °C, Time 3.629e+6 sec	702 % @Treatment Temp. 248 °F, Time 1008 hour	heat aging; ASTM D573-99
Compression Set	20 % @Temperature 23.0 °C, Time 79200 sec	20 % @Temperature 73.4 °F, Time 22.0 hour	ASTM D395

Processing Properties	Metric	English	Comments
Feed Temperature	170 °C	338 °F	extrusion
	180 °C	356 °F	injection
Nozzle Temperature	205 °C	401 °F
Adapter Temperature	190 °C	374 °F
Die Temperature	190 °C	374 °F
Melt Temperature	190 °C	374 °F	extrusion
	205 °C	401 °F	injection
Mold Temperature	10.0 - 30.0 °C	50.0 - 86.0 °F
Drying Temperature	80.0 °C	176 °F
Dry Time	2 - 4 hour	2 - 4 hour
Moisture Content	<= 0.030 %	<= 0.030 %
Back Pressure	0.350 MPa	50.8 psi

Descriptive Properties	Value	Comments
Injection Speed	fast