Multibase Nylex™ 2185 HFX Natural Polyamide + PP
| Category | Polymer , Thermoplastic , Nylon , Polypropylene (PP) |
| Manufacturer | Multibase |
| Trade Name | Nylex™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Multibase Nylex™ 2185 HFX Natural Polyamide + PP.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Forms: PelletsProcessing Methods:Injection moldingFeatures:Tensile Strength, HighInformation provided by Multibase
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.972 g/cc | 0.972 g/cc | ASTM 792 |
| Linear Mold Shrinkage | 0.012 cm/cm | 0.012 in/in | ASTM D955 |
| Melt Flow | 4.7 g/10 min @Load 2.16 kg, Temperature 230 °C |
4.7 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 44.1 MPa | 6400 psi | ASTM D638 |
| Elongation at Break | 27 % | 27 % | ASTM D638 |
| Flexural Strength | 66.9 MPa | 9700 psi | ASTM D790 |
| Flexural Modulus | 2.10 GPa | 305 ksi | Method I (3 point load), Procedure B); ASTM D790 |
| Izod Impact, Notched | 0.534 J/cm | 1.00 ft-lb/in | 73°F; ASTM D256 |
| Gardner Impact | 2.260 J | 1.667 ft-lb | ASTM D3029 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 141 °C | 286 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 77.2 °C | 171 °F | Unannealed; ASTM D648 |
| Vicat Softening Point | 161 °C | 322 °F | ASTM D1525 |
Users viewing this material also viewed the following:
- RheTech Products P252-01 Polypropylene Copolymer, Black
- PolyOne Bergamid™ A70 G50 HW SO Polyamide 66 (Nylon 66)
- DuPont Performance Polymers Crastin® CE2055 NC010 PBT (Unverified Data**)
- LNP Stat-Kon® PDX-S-90398 Polyamide 12, Stainless Steel Fiber (discontinued **)
- Kolon KOPA® KN163HI High Impact Nylon 6
- Saint-Gobain COHRlastic® R10480 Medium Low Compression Set Silicone Sponge Rubber
- Colorite Polymers CS9040UL Wire and Cable Jacket Vinyl Compound
- Aclo Accutech Polypropylene Copolymer CP0436W40L1 Wollastonite Reinforced
- Techmer Lehvoss Compounds Luvotech™ J-4/30/V0 NAT PA6/12 (discontinued **)
- Phenolic 40%, Carbon fabric 60%
Copyright © lookpolymers.com All Rights Reserved