Lehmann & Voss LUVOCOM® 1105-7766 PEEK, with carbon fiber, easy flowing
| Category | Polymer , Thermoplastic , Polyketone , Polyetheretherketone (PEEK) , Polyetheretherketone, PEEK, Carbon Fiber Filled |
| Manufacturer | Lehmann & Voss & Co. |
| Trade Name | LUVOCOM® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lehmann & Voss LUVOCOM® 1105-7766 PEEK, with carbon fiber, easy flowing.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.High-strength and high-stiff parts; low coefficient of expansion.Dynamic stressed parts at high movement velocity.Chemical and hydrolysis resistance parts, non flammable.Electrically conductive, suitable for continuous discharging of statically generated electricity.Bearings, sleeves, control disks, gear wheels, pump impellers, gear parts.Information provided by Lehmann & Voss & Co.KG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.42 g/cc | 1.42 g/cc | ISO 1183 |
| Water Absorption | <= 0.10 % | <= 0.10 % | 23°C/24h |
| Linear Mold Shrinkage | 0.00050 - 0.0020 cm/cm | 0.00050 - 0.0020 in/in | |
| Melt Flow | 21.3 g/10 min @Load 2.16 kg, Temperature 380 °C |
21.3 g/10 min @Load 4.76 lb, Temperature 716 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Stress | 260 MPa | 37700 psi | |
| Elongation at Yield | 1.6 % | 1.6 % | |
| 2.1 % | 2.1 % | flexural | |
| Modulus of Elasticity | 27.0 GPa | 3920 ksi | |
| Flexural Strength | 375 MPa | 54400 psi | |
| Flexural Modulus | 22.95 GPa | 3329 ksi | |
| Charpy Impact Unnotched | 2.50 J/cm² | 11.9 ft-lb/in² | flatwise; ISO 179 1fU |
| Charpy Impact, Notched | 0.700 J/cm² | 3.33 ft-lb/in² | ISO 179 1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 9.00 µm/m-°C | 5.00 µin/in-°F | DIN 53752 |
| Thermal Conductivity | 0.600 W/m-K | 4.16 BTU-in/hr-ft²-°F | DIN 52612 |
| Maximum Service Temperature, Air | 250 °C | 482 °F | |
| 280 °C | 536 °F | short term | |
| Deflection Temperature at 1.8 MPa (264 psi) | 260 °C | 500 °F | |
| Vicat Softening Point | 320 °C | 608 °F | DIN ISO 306 |
| Flammability, UL94 | V-0 | V-0 | not recognized by UL |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | <= 10000 ohm | <= 10000 ohm | |
| Insulation Resistance | <= 100000 ohm | <= 100000 ohm |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 390 °C | 734 °F | mass temp |
| Nozzle Temperature | 360 - 380 °C | 680 - 716 °F | |
| Zone 1 | 360 - 370 °C | 680 - 698 °F | |
| Zone 2 | 380 - 390 °C | 716 - 734 °F | |
| Zone 3 | 390 - 400 °C | 734 - 752 °F | |
| Mold Temperature | 170 - 200 °C | 338 - 392 °F | |
| Drying Temperature | 120 °C @Time 21600 - 28800 sec |
248 °F @Time 6.00 - 8.00 hour |
or |
| 150 °C @Time 10800 - 21600 sec |
302 °F @Time 3.00 - 6.00 hour |
Dehumidifying dryer |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | black |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Cycoloy® CE8510 PC+ABS (Europe-Africa-Middle East)
- Lanxess Durethan® CI 31 F 000000 Copolyamide PA6/6I
- Schott N-SF10 Glass
- Dow Corning SILASTIC® 9252/150P A&B KIT
- Dow Corning SILASTIC® HV 1666/65 GRAY SILICONE RUBBER
- DuPont Teijin Films Melinex® 376 Polyester Film
- CMW® THERMKON® 83 Tungsten Copper parts
- PolyOne Edgetek® ES-20GF/000 Polyethersulfone, Glass Filled (discontinued **)
- Adell ER-17 Homopolymer Polypropylene, 30% Glass Reinforced
- SABIC Innovative Plastics Cycolac® CRT3370F ABS (Europe-Africa-Middle East)
Copyright © lookpolymers.com All Rights Reserved