Multibase Multi-Pro® 1010 T Black 10% Talc Content Polypropylene
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 10% Talc Filler |
| Manufacturer | Multibase |
| Trade Name | Multi-Pro® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Multibase Multi-Pro® 1010 T Black 10% Talc Content Polypropylene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PPH talc filled compound suitable for containers and wash-tubs requiring elevated stiffness and improved cycle times.Data provided by Multibase.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.974 g/cc | 0.0352 lb/in³ | ASTM D792-91 |
| Melt Flow | 11 g/10 min | 11 g/10 min | (Condition L) ASTM D-1238-94a |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 33.8 MPa | 4900 psi | ASTM D638-95 |
| Elongation at Break | 60 % | 60 % | ASTM D638-95 |
| Flexural Strength | 46.9 MPa | 6800 psi | ASTM D790-92 |
| Flexural Modulus | 2.00 GPa | 290 ksi | Method 1, Proc. B; ASTM D-790-95 |
| Izod Impact, Notched | 0.480 J/cm | 0.899 ft-lb/in | ASTM D256-93a |
| Gardner Impact | 0.700 J | 0.516 ft-lb | ASTM D5420-93 |
Users viewing this material also viewed the following:
- MV Labs OS450 (NH4)2OsCl6 Ammonium hexachloroosmate(IV)
- NOVA Chemicals EPS 33MBHD Modified Expandable Polystyrene
- NOVA Chemicals Novapol® PF-Y821-D Butene LLDPE Film Resin (discontinued **)
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 120 PHR N220 Filler
- Multibase Multi-Flex® TPE A 6001 BLK
- Heatbath/Park High Speed 75 Steel Brazing Neutral Salt
- Teknor Apex Monprene® MP-2235 Thermoplastic Elastomer
- Solvay MIRASHEEN® A-220 Surfactant
Copyright © lookpolymers.com All Rights Reserved