Multibase Multi-Flex® TPE D 6606 BLK
| Category | Polymer , Thermoplastic , Elastomer, TPE , Thermoplastic Elastomer, Melt-Processible Rubber |
| Manufacturer | Multibase |
| Trade Name | Multi-Flex® TPE |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Multibase Multi-Flex® TPE D 6606 BLK.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
The burn rate is 1 in/min (25 mm/min) based on ASTM FM VSS 302. Multi-Flex TPE contains Kraton™ G.Data provided by Multibase.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.16 g/cc | 0.0419 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.012 cm/cm | 0.012 in/in | ASTM D955 |
| Melt Flow | 5.0 - 9.0 g/10 min | 5.0 - 9.0 g/10 min | (Condition L) ASTM D-1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 63 | 63 | 10 sec; ASTM D-2240 |
| Tensile Strength, Ultimate | >= 15.2 MPa | >= 2200 psi | ASTM D412 |
| Elongation at Break | >= 100 % | >= 100 % | ASTM D412 |
| Flexural Modulus | >= 1.10 GPa | >= 160 ksi | method 1, Proc.B; ASTM D-790 |
| Tear Strength | 92.8 kN/m | 530 pli | ASTM D624 |
Users viewing this material also viewed the following:
- MV Labs MN820 MnO2 Manganese(IV) oxide
- Fiberfil® FV-31 Nylon 6, 31% Glass Reinforced, Heat Stabilized
- McDanel Advanced Ceramics MV-20 Mullite
- LG Chemical LUPOY GP5100 PC/ABS+GF10%
- Iran Petrochemical (PCC) Arak I2 HDPE
- Momentive Performance Materials RTV5223 Black Adhesive Sealant, Low Modulus Paste
- SABIC Innovative Plastics LNP LUBRICOMP RFP38 PA6.6
- Styrolution Polystyrol 143 E GR 21 PS
- Resinlab® EP1199 Black Unfilled Epoxy Adhesive
Copyright © lookpolymers.com All Rights Reserved