Momentive Performance Materials RTV630 Blue General Purpose Potting/Encapsulating Compound

Category	Polymer , Thermoset , Rubber or Thermoset Elastomer (TSE) , Silicone , Silicone, RTV, Encapsulation Grade
Manufacturer	Momentive Performance Materials (Former GE Silicones)
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Momentive Performance Materials RTV630 Blue General Purpose Potting/Encapsulating Compound.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Two-part addition cure. Two-part addition cure RTV silicones can be cured very quickly with the use of high heat. Addition cure products have no cure by-products and can be used to unlimited depths. Typical uses: high strength encapsulation.Data provided by the manufacturer, GE Silicones.GE Silicones became a part of Momentive Performance Materials in 2006.

Physical Properties	Metric	English	Comments
Density	1.28 g/cc	0.0462 lb/in³
Viscosity	150000 cP @Temperature 25.0 °C	150000 cP @Temperature 77.0 °F

Mechanical Properties	Metric	English	Comments
Hardness, Shore A	60	60
Tensile Strength, Ultimate	5.69 MPa	825 psi
Elongation at Break	250 %	250 %
Tear Strength	20.0 kN/m	114 pli	Die B

Thermal Properties	Metric	English	Comments
CTE, linear	210 µm/m-°C @Temperature 20.0 °C	117 µin/in-°F @Temperature 68.0 °F
Thermal Conductivity	0.310 W/m-K	2.15 BTU-in/hr-ft²-°F
Maximum Service Temperature, Air	204 °C	399 °F	Continuous useful temperature.
Minimum Service Temperature, Air	-60.0 °C	-76.0 °F	Continuous useful temperature.

Electrical Properties	Metric	English
Electrical Resistivity	4.50e+15 ohm-cm	4.50e+15 ohm-cm
Dielectric Constant	3.2 @Frequency 1000 Hz	3.2 @Frequency 1000 Hz
Dielectric Strength	17.7 kV/mm @Thickness 1.91 mm	450 kV/in @Thickness 0.0750 in
Dissipation Factor	0.0060 @Frequency 1000 Hz	0.0060 @Frequency 1000 Hz

Processing Properties	Metric	English	Comments
Processing Temperature	25.0 °C	77.0 °F	Cure time 4 hours.
Pot Life	240 min @Temperature 25.0 °C	240 min @Temperature 77.0 °F