Mitsui APELâ„¢ APL5014DP Cyclo Olefin Copolymer (COC)
| Category | Polymer , Thermoplastic , Cyclo Olefin Polymer |
| Manufacturer | Mitsui Chemicals America |
| Trade Name | APEL™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Mitsui APELâ„¢ APL5014DP Cyclo Olefin Copolymer (COC).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
This material possesses many characteristics inherent in polyolefins such as excellent electrical insulating properties and outstanding moisture resistance. In addition, it features good melt processability/flowability, good clarity and transparency, high glass transition temperature (Tg), exceptional moisture impermeability, impressive gas barrier qualities and excellent chemical and heat resistance. This material is used in Optical Parts applications.Information provided by Mitsui Chemicals America, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.04 g/cc | 1.04 g/cc | ASTM D792 |
| Moisture Vapor Transmission | 0.0900 cc-mm/m²-24hr-atm | 0.229 cc-mil/100 in²-24hr-atm | 1 atm; ASTM D1249 |
| Linear Mold Shrinkage | 0.0060 cm/cm | 0.0060 in/in | MCI Method |
| Melt Index of Compound | 36 g/10 min @Load 2.16 kg, Temperature 260 °C |
36 g/10 min @Load 4.76 lb, Temperature 500 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 60.0 MPa | 8700 psi | ASTM D638 |
| Elongation at Break | 3.0 % | 3.0 % | ASTM D638 |
| Flexural Strength | 100 MPa | 14500 psi | ASTM D790 |
| Flexural Modulus | 3.20 GPa | 464 ksi | ASTM D790 |
| Izod Impact, Notched | 0.250 J/cm | 0.468 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched (ISO) | 10.0 kJ/m² | 4.76 ft-lb/in² | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 147 °C | 297 °F | TMA; MCI Method |
| Deflection Temperature at 1.8 MPa (264 psi) | 125 °C | 257 °F | ASTM D648 |
| Glass Transition Temp, Tg | 135 °C | 275 °F | MCI Method |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Refractive Index | 1.54 | 1.54 | ASTM D542 |
| Haze | 2.0 % | 2.0 % | ASTM D1003 |
| Transmission, Visible | 90 % | 90 % | ASTM D1003 |
Users viewing this material also viewed the following:
- Total Lacqtene® 2001 TYL 46 HDPE pipe (discontinued **)
- 3M Dyneon™ CC146/S Custom Fluoropolymer Compound (discontinued **)
- Garlock MULTI-SWELLâ„¢ 3760 Compressed Aramid Fiber Gasketing
- Teknor Apex APEX® 80855 Polyvinyl Chloride, Flexible
- Teknor Apex Telcar® OBC 4985A Thermoplastic Elastomer
- DuPont Performance Polymers Delrin® 111P NC010 Acetal Homopolymer
- Arlon 44576R016 0.016" (0.406 mm) Cured/Uncured Silicone Rubber with Fiberglass Substrate
- ConocoPhillips Hydroclear® 32 TCS Slideway lubricant
- Ineos Nova 5100 High Impact Polystyrene (discontinued **)
Copyright © lookpolymers.com All Rights Reserved