Mitsubishi Xantar® G6F 23 R Polycarbonate-30% Glass Reinforced

Category Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, 30% Glass Filled
Manufacturer Mitsubishi
Trade Name Xantar®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Mitsubishi Xantar® G6F 23 R Polycarbonate-30% Glass Reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Xantar® materials are engineered for performance, consistency and reliability. This makes Xantar® resins ideal for interior automotive components, electrical equipment and consumer appliances where quality is a key requirement. The Xantar® range includes: clear and tinted grades for transparent applicationsreinforced materialsFlame retardant and halogen free typeslubricated materials for added wear resistanceMitsubishi Engineering Plastics acquired the Xantar® product line from DSM in 2010.
Physical Properties Metric English Comments
Density 1.43 g/cc
0.0517 lb/in³
ISO 1183
Water Absorption 0.26 %
0.26 %
Sim. to ISO 62
Viscosity Test 48 cm³/g
48 cm³/g
Limiting Viscosity Number; ISO 1628-4
Linear Mold Shrinkage, Flow 0.0020 cm/cm
0.0020 in/in
ISO 294-4
Linear Mold Shrinkage, Transverse 0.0040 cm/cm
0.0040 in/in
ISO 294-4
Melt Flow 5.72 g/10 min

@Load 1.20 kg,
Temperature 300 °C
 5.72 g/10 min

@Load 2.65 lb,
Temperature 572 °F
 Calculated from Volume Flow Rate of 4 cm<sup>3</sup>/10min.; ISO 1133
Mechanical Properties Metric English Comments
Hardness, Rockwell M 91
91
ISO 2039-2
Tensile Strength at Break 110 MPa
16000 psi
ISO 527-1/-2
Elongation at Break 2.0 %
2.0 %
ISO 527-1/-2
Tensile Modulus 9.50 GPa
1380 ksi
ISO 527-1/-2
Flexural Strength 150 MPa
21800 psi
ISO 178
Flexural Modulus 7.00 GPa
1020 ksi
ISO 178
Izod Impact, Notched (ISO) 10.0 kJ/m²

@Temperature 23.0 °C
 4.76 ft-lb/in²

@Temperature 73.4 °F
 ISO 180/4A
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 25.0 µm/m-°C

@Temperature 20.0 °C
 13.9 µin/in-°F

@Temperature 68.0 °F
 ISO 11359-1/-2
Maximum Service Temperature, Air 125 °C
257 °F
Ball Pressure Temperature; IEC 60695-10-2
Deflection Temperature at 1.8 MPa (264 psi) 145 °C
293 °F
ISO 75-1/-2
Vicat Softening Point 152 °C
306 °F
50°C/h 50N; ISO 306
UL RTI, Electrical 130 °C

@Thickness 1.50 mm
 266 °F

@Thickness 0.0591 in
 UL746B
130 °C

@Thickness 3.00 mm
 266 °F

@Thickness 0.118 in
 UL746B
UL RTI, Mechanical with Impact 125 °C

@Thickness 1.50 mm
 257 °F

@Thickness 0.0591 in
 UL746B
130 °C

@Thickness 3.00 mm
 266 °F

@Thickness 0.118 in
 UL746B
UL RTI, Mechanical without Impact 125 °C

@Thickness 1.50 mm
 257 °F

@Thickness 0.0591 in
 UL746B
130 °C

@Thickness 3.00 mm
 266 °F

@Thickness 0.118 in
 UL746B
Flammability, UL94 V-0

@Thickness 1.60 mm
 V-0

@Thickness 0.0630 in
 IEC 60695-11-10
V-0

@Thickness 3.00 mm
 V-0

@Thickness 0.118 in
 IEC 60695-11-10
Oxygen Index 36 %
36 %
ISO 4589-1/-2
Glow Wire Test 850 °C

@Thickness 1.50 mm
 1560 °F

@Thickness 0.0591 in
 Glow Wire Ignition Temperature; IEC 60695-2-13
875 °C

@Thickness 3.00 mm
 1610 °F

@Thickness 0.118 in
 Glow Wire Ignition Temperature; IEC 60695-2-13
960 °C

@Thickness 3.00 mm
 1760 °F

@Thickness 0.118 in
 Glow Wire Flammability Index; IEC 60695-2-12
960 °C

@Thickness 1.50 mm
 1760 °F

@Thickness 0.0591 in
 Glow Wire Flammability Index; IEC 60695-2-12
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+15 ohm-cm
>= 1.00e+15 ohm-cm
IEC 60093
Surface Resistance >= 1.00e+15 ohm
>= 1.00e+15 ohm
IEC 60093
Dielectric Constant 3.4

@Frequency 100 Hz
 3.4

@Frequency 100 Hz
 IEC 60250
3.4

@Frequency 1e+6 Hz
 3.4

@Frequency 1e+6 Hz
 IEC 60250
Dielectric Strength 29.0 kV/mm
737 kV/in
IEC 60243-1
Dissipation Factor 0.00090

@Frequency 100 Hz
 0.00090

@Frequency 100 Hz
 IEC 60250
0.0090

@Frequency 1e+6 Hz
 0.0090

@Frequency 1e+6 Hz
 IEC 60250
Comparative Tracking Index 200 V
200 V
IEC 60112
175 - 249 V
175 - 249 V
PLC 3; UL 746A
Descriptive Properties Value Comments
Flame Retardant Yes
Flame Retarding Agent Yes
Heat stabilized or stable to heat Yes
Injection molding Yes
Release Agent Yes
With Fillers Yes