Mitsubishi Hostaphan® RN, 23 micron Nominal Thickness Universal Polyethylene Terephthalate Film
| Category | Polymer , Film , Thermoplastic , Polyester, TP , Polyethylene Terephthalate (PET) , Polyethylene Terephthalate (PET), Unreinforced |
| Manufacturer | Mitsubishi |
| Trade Name | Hostaphan® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Mitsubishi Hostaphan® RN, 23 micron Nominal Thickness Universal Polyethylene Terephthalate Film.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Hostaphan® RN is a transparent, biaxially oriented film made of polyethylene terephthalate (PET) and characterized by outstanding physical properties. Hostaphan® RN is the standard product for the following applications:Films for packagingCoatingLaminatingMetallizingPrintingDecorative filmsGloss laminationsAdhesive tapesInsulation tapesReleaseTransfer filmRelease film for thermosetting resingsHot stamping/Roll leafInformation provided by Mitsubishi Polyester Film
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.40 g/cc @Temperature 23.0 °C |
0.0506 lb/in³ @Temperature 73.4 °F |
ASTM D1505-68, method C |
| Linear Mold Shrinkage | 0.013 cm/cm @Temperature 150 °C, Time 900 sec |
0.013 in/in @Temperature 302 °F, Time 0.250 hour |
DIN 40634 |
| Linear Mold Shrinkage, Transverse | 0.0010 cm/cm @Temperature 150 °C, Time 900 sec |
0.0010 in/in @Temperature 302 °F, Time 0.250 hour |
DIN 40634 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Tensile Strength at Yield, MD | 230 MPa | 33400 psi | Test speed 100%/min.; 50% r.h.; ISO 527-1, ISO 527-3; Sample type 2 |
| Film Tensile Strength at Yield, TD | 260 MPa | 37700 psi | Test speed 100%/min.; 50% r.h.; ISO 527-1, ISO 527-3; Sample type 2 |
| Film Elongation at Break, MD | >= 110 % | >= 110 % | Test speed 100%/min.; 50% r.h.; ISO 527-1, ISO 527-3; Sample type 2 |
| Film Elongation at Break, TD | 100 % | 100 % | Test speed 100%/min.; 50% r.h.; ISO 527-1, ISO 527-3; Sample type 2 |
| Modulus of Elasticity | 4.40 GPa @Temperature 23.0 °C |
638 ksi @Temperature 73.4 °F |
MD; Test speed 1%/min.; 50% r.h.; ISO 527-1, ISO 527-3; Sample type 2 |
| 5.00 GPa @Temperature 23.0 °C |
725 ksi @Temperature 73.4 °F |
TD; Test speed 1%/min.; 50% r.h.; ISO 527-1, ISO 527-3; Sample type 2 | |
| Coefficient of Friction, Static | 0.40 | 0.40 | DIN 53375 or ASTM D1894 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 7.0 % | 7.0 % | Enlarged measurement angle; ASTM D1003-61, method A |
| Transmission, Visible | 90 % | 90 % | transparent; thickness not quantified |
| Descriptive Properties | Value | Comments |
|---|---|---|
| F5-value (MPa) | 105 | ISO 527-1, ISO 527-3; Sample type 2; TD; Test speed 100%/min.; 23ºC, 50% r.h. |
| 110 | ISO 527-1, ISO 527-3; Sample type 2; MD; Test speed 100%/min.; 23ºC, 50% r.h. |
Users viewing this material also viewed the following:
- Nye Lubricants 700B (RT) Synthetic Oil
- Master Bond EP36CLV One Component Heat Resistant Liquid Flexible Epoxy
- Unifrax Excelfrax® 1800 Flexliner Microporous Insulation
- Hexcel® HexWeb® HRH-10 - 3/8 - 1.5 Aramid Fiber/Phenolic Resin Honeycomb
- Ensinger Tecapeek® CF30 Polyetheretherketone, 30% Carbon Reinforced (PEEK)
- DuPont Performance Polymers Hytrel® HTR8685 BK022A Polyester Elastomer TPC-ET (Unverified Data**)
- 3M 3W26X Protective UV Tape
- LNP ULTEM® SMU5835 Polyetherimide, 25% Carbon Fiber Reinforcement (discontinued **)
- Samyang Tribit® 1800H PBT, Extruding Formality
Copyright © lookpolymers.com All Rights Reserved