Menzolit Menzolit® SMC 2600 Unsaturated Polyester UP
| Category | Polymer , Thermoset , Polyester, TS , Thermoset Polyester Glass SMC |
| Manufacturer | Menzolit |
| Trade Name | Menzolit® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Menzolit Menzolit® SMC 2600 Unsaturated Polyester UP.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
SMC 2600 is a special SMC with electrically conductive properties. Because of its conductivity, SMC 2600 is antistatic and prevents build-up of electrical charges on the surface. Despite of its conductivity the electrical properties are still good enough to provide an electrical isolation to power circuits. The glass level has been selected to combine good mouldability with good strength and stiffness properties. Typical applications are housings and covers within telecommunication, electrical industry, office equipment as well as ex-proof applications within the mining or oil/gas exploration industry.Information Provided by Menzolit
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.80 g/cc | 0.0650 lb/in³ | ISO 1183 |
| Water Absorption | <= 0.50 % | <= 0.50 % | ISO 62 |
| Linear Mold Shrinkage | 0.0015 cm/cm | 0.0015 in/in | ISO 2577 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 75.0 MPa @Temperature 22.0 °C |
10900 psi @Temperature 71.6 °F |
25mm flat samples, compression moulded; ISO 527-4 |
| Tensile Strength, Yield | 75.0 MPa @Temperature 22.0 °C |
10900 psi @Temperature 71.6 °F |
25mm flat samples, compression moulded; ISO 527-4 |
| Elongation at Yield | 0.00 % | 0.00 % | tensile rupture strain; ISO 527-4 |
| Modulus of Elasticity | 12.0 GPa | 1740 ksi | 25mm flat samples, compression moulded; ISO 527-4 |
| Flexural Strength | 179 MPa @Temperature 22.0 °C |
26000 psi @Temperature 71.6 °F |
25 mm wide 100 mm long, flat samples; ISO 14125 |
| Flexural Modulus | 10.0 GPa @Temperature 22.0 °C |
1450 ksi @Temperature 71.6 °F |
25 mm wide 100 mm long, flat samples; ISO 14125 |
| Poissons Ratio | 0.30 | 0.30 | |
| Shear Modulus | 4.60 GPa | 667 ksi | in plane |
| Charpy Impact, Notched | 8.10 J/cm² | 38.5 ft-lb/in² | ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 12.0 µm/m-°C | 6.67 µin/in-°F | ISO 11359-2 |
| Specific Heat Capacity | 1.10 J/g-°C | 0.263 BTU/lb-°F | |
| Thermal Conductivity | 0.700 W/m-K | 4.86 BTU-in/hr-ft²-°F | |
| Maximum Service Temperature, Air | 165 °C | 329 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | >= 200 °C | >= 392 °F | ISO 75-2 |
| Minimum Service Temperature, Air | -40.0 °C | -40.0 °F | |
| Glass Transition Temp, Tg | 170 °C | 338 °F | ISO 11357-2 |
| Flammability, UL94 | V-0 @Thickness 3.00 mm |
V-0 @Thickness 0.118 in |
|
| Oxygen Index | 30 % | 30 % | ISO 4589-2 |
| Glow Wire Test | 960 °C | 1760 °F | IEC 60695-2-12 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+11 ohm-cm | 1.00e+11 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+8 ohm | 1.00e+8 ohm | IEC 60093 |
| Dielectric Strength | >= 0.250 kV/mm | >= 6.35 kV/in | IEC 60243-1 |
| Comparative Tracking Index | 600 V | 600 V | IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 135 - 150 °C | 275 - 302 °F | Compression moulding, matched metal die |
Users viewing this material also viewed the following:
- NOVA Chemicals DYLARK® 480 Impact Grade Engineering Resin
- PolyOne Dynaflex™ G7950-1001-00 Thermoplastic Elastomer (TPE)
- LATI Latiohm 57-05 PD01 G/15 PPA, 15% Glass Fiber Reinforced
- SK Chemicals SKYTHANE® 180A R series Polyurethane
- UBE 1022T Nylon 6 Monofilament (Drawing Ratio=4.8)
- Cossa Polimeri ESTACARB 0501 Polycarbonate
- Cytec (Conap) FR-2000 / FR-200 Conapoxy® Resin / Conacure® Hardener
- Daikin NEOFLON AP-221SH PFA Semiconductor Grade
- Carpenter Custom 450® Stainless Steel, Condition H1150 (Age Hardened 621°C)
- Arkema Group Pebax® MX 1205 SN 01 Polyether Block Amide (PEBA) (Conditioned)
Copyright © lookpolymers.com All Rights Reserved