- Samyang Tribit® 1550GN30 PBT Alloy, Reinforced Flame Retardancy
Samyang Tribit® 1550GN30 PBT Alloy, Reinforced Flame Retardancy
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), Flame Retardant |
| Manufacturer | Samyang |
| Trade Name | Tribit® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Samyang Tribit® 1550GN30 PBT Alloy, Reinforced Flame Retardancy.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Crystallization is fast, formability is excellent and thermal resistance, chemical resistance, electrical properties and abrasion resistance are excellent.1550GN30 is a reinforced, flame retardant (ALLOY) grade.Applications: Connectors (insulation characteristics)Information provided by Samyang.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.59 g/cc | 1.59 g/cc | ASTM D792 |
| Water Absorption | 0.070 % | 0.070 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0020 - 0.012 cm/cm | 0.0020 - 0.012 in/in | ASTM D955 |
| Melt Flow | 48 g/10 min @Load 2.16 kg, Temperature 250 °C |
48 g/10 min @Load 4.76 lb, Temperature 482 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 120 | 120 | ASTM D785 |
| Tensile Strength | 123 MPa | 17800 psi | ASTM D638 |
| Elongation at Break | 2.0 % | 2.0 % | ASTM D638 |
| Flexural Yield Strength | 147 MPa | 21300 psi | ASTM D790 |
| Flexural Modulus | 7.16 GPa | 1040 ksi | ASTM D790 |
| Izod Impact, Notched | 0.588 J/cm @Thickness 3.17 mm |
1.10 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 30.0 µm/m-°C | 16.7 µin/in-°F | ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 225 °C | 437 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 210 °C | 410 °F | ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 0.710 mm |
V-0 @Thickness 0.0280 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 |
| Dielectric Constant | 3.2 | 3.2 | ASTM D150 |
| Dielectric Strength | 20.0 kV/mm | 508 kV/in | ASTM D149 |
| Dissipation Factor | 0.016 | 0.016 | ASTM D150 |
| Arc Resistance | 110 sec | 110 sec | ASTM D495 |
Users viewing this material also viewed the following:
- PEAK Werkstoff DISPAL S541 Aluminum Alloy, AlMg6Mn4SiTiZr, Condition F
- Global XNY-1424 Easy Flow Polycarbonate/Polyester Alloy
- Kostat ICP-STAT ICS-1002 PP Sheet
- Lucent Polymers GPB-130 Polybutylene Terephthalate, 30% Glass Fiber Reinforced
- Lushan PF-300 Adhesive Resin for Multi-layer Barrier Composite Sheet
- SABIC Innovative Plastics LNP THERMOCOMP QF006 PA 6/10
- Sichuan Deyang Haton® hMR61LC1 Polyphenylene Sulfide, Glass & Mineral Reinforced
- Arkema Group Rilsan® AMN Y TLD Nylon 12, MoS2 Filled (Conditioned)
- Addiplast Addilene J 110 Polypropylene Copolymer
Copyright © lookpolymers.com All Rights Reserved