- Materion AlBeCastâ„¢ IC910 Aluminum Beryllium Composite
Materion AlBeCastâ„¢ IC910 Aluminum Beryllium Composite
| Category | Metal , Metal Matrix Composite , Nonferrous Metal , Beryllium Alloy |
| Manufacturer | Materion Corporation (former Brush Wellman) |
| Trade Name | AlBeCast™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Materion AlBeCastâ„¢ IC910 Aluminum Beryllium Composite.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Mechanical properties are typical values at RT. AlBeCastâ„¢ IC910 is an aluminum-beryllium alloy that combines the advantages of a net shape casting technology, investment casting, with the stiffness, thermal performance, and weight savings of Al/Be materials. The casting process requires little change from Al or Ti casting.Please note that there are health hazards associated with beryllium, especially when present as airborne particles generated during processing. As with any material, be aware of hazards and take steps to reduce exposure to a safe level.Information provided by Brush Wellman.Brush Engineered Materials Inc. changed its name to Materion Corporation in March 2011.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 2.17 g/cc | 0.0784 lb/in³ |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 207 MPa | 30000 psi | |
| Tensile Strength, Yield | 158 MPa @Strain 0.200 % |
22900 psi @Strain 0.200 % |
|
| Elongation at Break | 4.0 % | 4.0 % | |
| Modulus of Elasticity | 193 GPa | 28000 ksi | in tension. Dynamic modulus is 192 GPa. |
| Compressive Yield Strength | 147 MPa | 21300 psi | |
| Poissons Ratio | 0.154 | 0.154 | |
| Fatigue Strength | 117 MPa @# of Cycles 1.00e+7 |
17000 psi @# of Cycles 1.00e+7 |
R=0.05; Kt = 2.16 MPa |
| Fracture Toughness | 7.30 - 14.6 MPa-m½ | 6.64 - 13.3 ksi-in½ | K<sub>Q</sub> |
| Shear Modulus | 84.0 GPa | 12200 ksi | dynamic |
| Shear Strength | 181 MPa | 26300 psi | double pin shear (ASTM B-789) |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 14.6 µm/m-°C @Temperature 20.0 °C |
8.11 µin/in-°F @Temperature 68.0 °F |
|
| 16.0 µm/m-°C @Temperature 250 °C |
8.89 µin/in-°F @Temperature 482 °F |
||
| 18.2 µm/m-°C @Temperature 500 °C |
10.1 µin/in-°F @Temperature 932 °F |
||
| Specific Heat Capacity | 1.56 J/g-°C | 0.373 BTU/lb-°F | |
| Thermal Conductivity | 110 W/m-K | 763 BTU-in/hr-ft²-°F |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Aluminum, Al | 38 % | 38 % | As remainder |
| Beryllium, Be | 57 - 63 % | 57 - 63 % | |
| Iron, Fe | <= 0.30 % | <= 0.30 % | |
| Nickel, Ni | 2.1 - 3.4 % | 2.1 - 3.4 % | |
| Oxygen, O | <= 0.24 % | <= 0.24 % | |
| Silicon, Si | <= 0.50 % | <= 0.50 % |
Users viewing this material also viewed the following:
- Plaskolite Duraplex® SG-05 Sign Grade Acrylic Sheet, Impact Modified
- PolyOne Geon™ 140 Series 140X484 Polyvinyl Chloride Homopolymer (PVC Homopolymer)
- SABIC Innovative Plastics Cycoloy® C6800 PC+ABS
- SABIC Innovative Plastics LNP LUBRICOMP OX90351 PPS
- Teknor Apex Telcar® TL-2478K Thermoplastic Elastomer
- Wellman Wellamid® T423-BK10 Mineral Reinforced Nylon 6, Heat Stabilized
- Formosa Plastics Formolon® 622R PVC
- A. Schulman POLYBATCH™ White P80754PF Concentrate Based In Polypropylene
- Ecomass® 1850ZC84 Stainless Steel Powder Filled Polyamide (PA6), Injection Molding
- Amity Thermosets ATE 183 M Phenolic Molding Mica and organic Filler, Compression Molded
Copyright © lookpolymers.com All Rights Reserved