SABIC Innovative Plastics LNP VERTON UX03320 PPA (Asia Pacific)

Category Polymer , Thermoplastic , Polyphthalamide (PPA)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP VERTON
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP VERTON UX03320 PPA (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
VERTON* UX03320 is a compound based on Polyphthalamide resin containing Long Glass.
Physical Properties Metric English Comments
Density 1.63 g/cc
0.0589 lb/in³
ASTM D792
1.63 g/cc
0.0589 lb/in³
ISO 1183
Moisture Absorption 0.200 %
0.200 %
50% RH, 24 hrs; ASTM D570
0.300 %
0.300 %
23°C / 50% RH; ISO 62
Linear Mold Shrinkage, Flow 0.00060 cm/cm

@Time 86400 sec
 0.00060 in/in

@Time 24.0 hour
 ISO 294
0.00050 - 0.0010 cm/cm

@Time 86400 sec
 0.00050 - 0.0010 in/in

@Time 24.0 hour
 ASTM D955
Linear Mold Shrinkage, Transverse 0.00080 - 0.0020 cm/cm

@Time 86400 sec
 0.00080 - 0.0020 in/in

@Time 24.0 hour
 ASTM D955
0.0015 cm/cm

@Time 86400 sec
 0.0015 in/in

@Time 24.0 hour
 ISO 294
Spiral Flow 30.0 cm

@Thickness 1.00 mm
 11.8 in

@Thickness 0.0394 in
 SABIC Method
70.0 cm

@Thickness 3.00 mm
 27.6 in

@Thickness 0.118 in
 SABIC Method
Mechanical Properties Metric English Comments
Tensile Strength at Break 200 MPa
29000 psi
ISO 527
220 MPa
31900 psi
ASTM D638
Elongation at Break 1.9 %
1.9 %
ISO 527
1.9 %
1.9 %
ASTM D638
Tensile Modulus 18.2 GPa
2640 ksi
5 mm/min; ASTM D638
20.3 GPa
2940 ksi
1 mm/min; ISO 527
Flexural Strength 300 MPa
43500 psi
ASTM D790
360 MPa
52200 psi
2 mm/min; ISO 178
360 MPa
52200 psi
ISO 178
Flexural Modulus 17.7 GPa
2570 ksi
2 mm/min; ISO 178
17.7 GPa
2570 ksi
ISO 178
18.0 GPa
2610 ksi
ASTM D790
Izod Impact, Notched 3.00 J/cm
5.62 ft-lb/in
ASTM D256
Izod Impact, Unnotched 8.00 J/cm
15.0 ft-lb/in
ASTM D4812
Izod Impact, Notched (ISO) 38.0 kJ/m²
18.1 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 70.0 kJ/m²
33.3 ft-lb/in²
80*10*4; ISO 180/1U
Dart Drop, Total Energy 15.0 J

@Temperature 23.0 °C
 11.1 ft-lb

@Temperature 73.4 °F
 ASTM D3763
Impact Test 19.0 J
14.0 ft-lb
Multiaxial Impact; ISO 6603
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 12.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 6.67 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
12.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 6.67 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
CTE, linear, Transverse to Flow 22.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 12.2 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
22.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 12.2 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
Deflection Temperature at 1.8 MPa (264 psi) 275 °C
527 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
260 °C

@Thickness 3.20 mm
 500 °F

@Thickness 0.126 in
 unannealed; ASTM D648
Flammability, UL94 HB

@Thickness 0.800 mm
 HB

@Thickness 0.0315 in
 UL 94