LyondellBasell Alathon® L5008HP High Density Polyethylene, Pressure Pipe Extrusion Grade
| Category | Polymer , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Pipe Grade |
| Manufacturer | LyondellBasell (former Equistar) |
| Trade Name | Alathon® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LyondellBasell Alathon® L5008HP High Density Polyethylene, Pressure Pipe Extrusion Grade.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
ALATHON L5008HP is a bimodal, high molecular weight, high density polyethylene resin with excellent processability designed to meet the high performance requirements of pressure pipe applications including gas distribution, industrial piping, gas gathering, municipal water service lines and sewer lines. When L5008HP is compounded with an Equistar approved black concentrate this formula meets the following standards.Plastics Pipe Institute (PPI) PE 4710 per ASTM D 3350-06Plastics Pipe Institute (PPI) PE 3408 per ASTM D 3350-02aNSF Standard 14 and Standard 61 for Potable Water Pipe and Fittings.ASTM D 3350 Cell Classification 445574C.Chemical Resistance per ASTM D 2513-01a, Section 5.4.This product is from the former Equistar product line.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.949 g/cc | 0.0343 lb/in³ | ASTM D1505 |
| Melt Flow | 0.070 g/10 min | 0.070 g/10 min | ASTM D1238 |
| 16 g/10 min | 16 g/10 min | High Load; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| PENT | >= 1500 hour @Temperature 80.0 °C |
>= 1500 hour @Temperature 176 °F |
2.4MPa |
| Tensile Strength at Break | 35.2 MPa | 5100 psi | ASTM D638 |
| Tensile Strength, Yield | 24.1 MPa | 3500 psi | ASTM D638 |
| Elongation at Break | 800 % | 800 % | ASTM D638 |
| 2% Secant Modulus | 1.01 GPa | 147 ksi | ASTM D790 |
| Hydrostatic Design Basis | 11.0 MPa | 1600 psi | ASTM D2837 |
| 6.89 MPa @Temperature 60.0 °C |
1000 psi @Temperature 140 °F |
ASTM D2837 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 76.0 °C | 169 °F | ASTM D648 |
| DSC Induction Temperature | 250 °C | 482 °F |
Users viewing this material also viewed the following:
- Kennametal Stellite Stellite® SF6 Cobalt Alloy
- Multibase Multi-Flex® RP 6568 C Natural TPE Thermoplastic Elastomer
- Solvay Specialty Polymers Radel® R-5800 Polyphenylsulfone (PPSU)
- Teknor Apex APEX® 90-A471R-80-NT Polyvinyl Chloride, Flexible
- Shinkong Synthetic Fibers Shinite® T101 PET
- SABIC Innovative Plastics LNP VERTON MV008 PP (Europe-Africa-Middle East)
- ExxonMobil LDPE LD 136.MN Low Density Polyethylene Resin
- Diamond Polymers ABSPC 7030 ABS/PC Injection Molding Grade, High Impact
- Atom Adhesives AA-BOND FDA26 Epoxy Adhesive
- Victrex® Vicote® F813 Black Polyetheretherketone (PEEK) Liquid Dispersion
Copyright © lookpolymers.com All Rights Reserved