Lucent Polymers GPB-130L Polybutylene Terephthalate, 30% Glass Fiber Reinforced
| Category | Polymer , Renewable/Recycled Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), 30% Glass Fiber Filled |
| Manufacturer | Lucent Polymers |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lucent Polymers GPB-130L Polybutylene Terephthalate, 30% Glass Fiber Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Recycled ContentAdd "R" for Added ReleaseAdd "U" for UV StabilizerInformation provided by Lucent Polymers, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.50 g/cc | 1.50 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0030 cm/cm @Thickness 3.17 mm |
0.0030 in/in @Thickness 0.125 in |
1/8" Section |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 117.24 MPa | 17004 psi | ASTM D638 |
| Elongation at Break | >= 3.0 % | >= 3.0 % | ASTM D638 |
| Flexural Strength | 158.62 MPa | 23006 psi | ASTM D790 |
| Flexural Modulus | 6.2069 GPa | 900.24 ksi | ASTM D790 |
| Izod Impact, Notched | 0.694 J/cm @Thickness 3.17 mm, Temperature 22.8 °C |
1.30 ft-lb/in @Thickness 0.125 in, Temperature 73.0 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 151.67 °C | 305.01 °F | ASTM D648 |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® HPF1 PC Copolymer
- Lucas-Milhaupt Premabraze 616 Silver Based Cadmium Free Filler Metal
- Solvay Chemicals SOLID CAUSTIC SODA MICROPEARLS
- Lubrizol Estane® UB601 Thermoplastic Polyurethane
- United Cast Bar Unibar 600-3 Continuously Cast Spheroidal Graphite Iron
- A. Schulman SCHULAMID® 66 MV3 Unreinforced Nylon 6/6
- A. Schulman POLYFORT™ FPP 1200 Calcium Carbonate-Filled Homopolymer Polypropylene
- ConocoPhillips EP Conolith® HT Grease NLGI NO. 1
- Advanced Polymer Alloys Alcryn® 2265 UT Melt Processable Rubber
- Aptek DI-STRATE 95217 Microwave/RF Foam Substrate
Copyright © lookpolymers.com All Rights Reserved