Lucent Polymers 66-41 Nylon 66, Toughened
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Impact Grade |
| Manufacturer | Lucent Polymers |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lucent Polymers 66-41 Nylon 66, Toughened.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Add "H" for Heat Stabilized Add "HU" for WeatherableTypical Properties, Dry as MoldedInformation provided by Lucent Polymers, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.09 g/cc | 1.09 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.016 cm/cm @Thickness 3.17 mm |
0.016 in/in @Thickness 0.125 in |
1/8" Section |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 57.93 MPa | 8402 psi | ASTM D638 |
| Elongation at Break | >= 30 % | >= 30 % | ASTM D638 |
| Flexural Strength | 65.52 MPa | 9503 psi | ASTM D790 |
| Flexural Modulus | 2.00 GPa | 290 ksi | ASTM D790 |
| Izod Impact, Notched | 1.602 J/cm @Thickness 3.17 mm, Temperature 22.8 °C |
3.001 ft-lb/in @Thickness 0.125 in, Temperature 73.0 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 250 - 265 °C | 482 - 509 °F | ASTM D789 |
| Deflection Temperature at 1.8 MPa (264 psi) | 72.22 °C | 162.0 °F | ASTM D648 |
Users viewing this material also viewed the following:
- Lehmann & Voss LUVOCOM® 1105-7741 PEEK, with mineral filler, lubricant modified
- Lucas-Milhaupt FOS FLO 7 Copper Phosphorus Alloy
- Haynes 188 alloy, 20% cold reduction, 3.2 mm thick sheet, 1120°C for 5 minutes
- Solvay Chemicals Hydrochloric Acid 31% - Technical Grade (11 wt% - 20 wt% Concentration)
- Sibur 15803-020 Low Density Polyethylene
- Techmer ES HiFill® PC GF20 X 20% Glass Filled
- Elastomer Engineering Elastamide 100 Elastomer Modified RIM Nylon 6
Copyright © lookpolymers.com All Rights Reserved