Lucas-Milhaupt HANDY HI-TEMP 095 Carbide Brazing Alloy

Category Metal , Nonferrous Metal , Copper Alloy , Solder/Braze Alloy
Manufacturer Lucas-Milhaupt
Trade Name HANDY HI-TEMP
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Lucas-Milhaupt HANDY HI-TEMP 095 Carbide Brazing Alloy.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Applications:Handy Hi-Temp 095 is a ductile copper-nickel-manganese filler metal designed for intermediate temperature brazing of carbides, cast irons, steel, stainless steels and nickel base heat-resistant alloys. This filler metal is ideally suited for combined brazing/heat-treating. It is useful in the brazing of materials that may be harmed by the higher temperatures used in copper brazing. It also may be used to advantage in the brazing of materials that are subject to erosion and grain-boundary penetration associated with high boron (2 to 5%) brazing filler metals. Characteristics:This filler metal is relatively free-flowing and will flow into long, narrow joints, except when solution of excessive amounts of nickel raises the liquidus temperature. Preferred joint clearances are in the range of 0.001 to 0.003 in. (3 to 8mm). Fluxless brazing may be accomplished in dry hydrogen or argon of at least -80EF (-62EC) dew point or by vacuum at 10-3 torr or better. Specifications:This filler metal conforms to the following specification-SAE AMS-4764 Information provided by Lucas-Milhaupt, Inc.
Physical Properties Metric English Comments
Density 7.67 g/cc
0.277 lb/in³
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 225 - 393 MPa

@Temperature 427 °C
32700 - 57000 psi

@Temperature 800 °F
304 Stainless Steel torch brazed butt joint
325 - 404 MPa

@Temperature 427 °C
47200 - 58600 psi

@Temperature 800 °F
304 Stainless Steel furnace brazed butt joint
354 - 412 MPa

@Temperature 23.0 °C
51300 - 59700 psi

@Temperature 73.4 °F
421 - 462 MPa

@Temperature 427 °C
61000 - 67000 psi

@Temperature 800 °F
4140 Carbon Steel torch brazed butt joint
371 - 590 MPa

@Temperature 23.0 °C
53800 - 85600 psi

@Temperature 73.4 °F
403 - 589 MPa

@Temperature 23.0 °C
58400 - 85400 psi

@Temperature 73.4 °F
Thermal Properties Metric English Comments
Melting Point 879.4 - 927 °C
1615 - 1700 °F
Solidus 879.4 °C
1615 °F
Melting Point
Liquidus 927 °C
1700 °F
Flow Point
Component Elements Properties Metric English Comments
Boron, B <= 0.10 %
<= 0.10 %
Copper, Cu 51.5 - 53.5 %
51.5 - 53.5 %
Iron, Fe <= 0.10 %
<= 0.10 %
Manganese, Mn >= 36.3 %
>= 36.3 %
Nickel, Ni 8.5 - 10.5 %
8.5 - 10.5 %
Other, total <= 0.50 %
<= 0.50 %
Electrical Properties Metric English Comments
Electrical Resistivity 0.000129 ohm-cm
0.000129 ohm-cm
Soft Wire
Processing Properties Metric English Comments
Processing Temperature 954 - 1090 °C
1750 - 2000 °F
Brazing Range
Descriptive Properties Value Comments
Color Reddish Gray