Lubrizol Estane® S160D Thermoplastic Polyurethane

Category	Polymer , Thermoplastic , Polyurethane, TP , Thermoplastic Polyurethane (TPUR), Polyester Grade
Manufacturer	Lubrizol (former Noveon)
Trade Name	ESTANE®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Lubrizol Estane® S160D Thermoplastic Polyurethane.pdf
Price	EMAIL US sales@lookpolymers.com

Material Notes:

Type: Estane® S160D is a Shore 63D, polyester based thermoplastic polyurethane (TPU). FDA approved (21 CFR 177.2600, 177.1680).Uses: Injection Molding.Availability: Americas, Europe, Middle East, Africa, India and Asia Information Provided by The Lubrizol Corporation

Physical Properties	Metric	English	Comments
Specific Gravity	1.25 g/cc	1.25 g/cc	ASTM D792
Linear Mold Shrinkage	0.0070 cm/cm	0.0070 in/in	ASTM D955

Mechanical Properties	Metric	English	Comments
Hardness, Shore D	63	63	ASTM D2240
Tensile Strength, Ultimate	44.1 MPa	6400 psi	ASTM D412
Tensile Strength, Yield	21.6 MPa	3130 psi	at 100% elongation; ASTM D412
	34.3 MPa	4980 psi	at 300% elongation; ASTM D412
Elongation at Break	480 %	480 %	ASTM D412
Tear Strength	226 kN/m	1290 pli	Die C; ASTM D624
Abrasion	25	25	mm<sup>3</sup> loss; ISO 4649
Compression Set	20 % @Temperature 23.0 °C, Time 79200 sec	20 % @Temperature 73.4 °F, Time 22.0 hour	ASTM D395
	45 % @Temperature 70.0 °C, Time 79200 sec	45 % @Temperature 158 °F, Time 22.0 hour	ASTM D395

Thermal Properties	Metric	English	Comments
Vicat Softening Point	158 °C	316 °F	ASTM D1525

Processing Properties	Metric	English
Feed Temperature	200 - 215 °C	392 - 419 °F
Nozzle Temperature	215 - 230 °C	419 - 446 °F
Mold Temperature	10.0 - 40.0 °C	50.0 - 104 °F
Drying Temperature	70.0 - 80.0 °C	158 - 176 °F
Dry Time	4.00 - 5.00 hour	4.00 - 5.00 hour
Injection Pressure	12.4 - 16.5 MPa	1800 - 2400 psi
Hold Pressure	8.96 - 13.1 MPa	1300 - 1900 psi
Back Pressure	0.207 - 0.552 MPa	30.0 - 80.0 psi
Cycle Time - Injection	25 - 30 sec	25 - 30 sec
Screw Speed	160 - 200 rpm	160 - 200 rpm

Descriptive Properties	Value	Comments
Injection time (s)	12-18