Lubrizol ESTALOC® 59104 Ester-Type, Reinforced Engineering Thermoplastic
| Category | Polymer , Thermoplastic , Elastomer, TPE , Polyurethane, TP , Thermoplastic Polyurethane, Elastomer, Polyester Grade |
| Manufacturer | Lubrizol (former Noveon) |
| Trade Name | ESTALOC® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lubrizol ESTALOC® 59104 Ester-Type, Reinforced Engineering Thermoplastic.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Features: Fast cycling, dimensional stability, durability, aesthetics, low temperature impactUses: Injection Molding Available in Americas and AsiaInformation provided by Lubrizol
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.31 g/cc | 1.31 g/cc | ASTM D792 |
| Maximum Moisture Content | 0.020 | 0.020 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 65 - 71 @Time 5.00 sec |
65 - 71 @Time 0.00139 hour |
ASTM D2240 |
| Tensile Strength | 40.0 MPa | 5800 psi | ASTM D638 |
| Elongation at Break | 40 % | 40 % | ASTM D638 |
| Flexural Strength | 47.0 MPa | 6820 psi | ASTM D790 |
| Flexural Modulus | 1.21 GPa | 175 ksi | ASTM D790 |
| Izod Impact, Notched | 6.94 J/cm | 13.0 ft-lb/in | ASTM D256 |
| 2.94 J/cm @Temperature -40.0 °C |
5.50 ft-lb/in @Temperature -40.0 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 95.0 °C | 203 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 61.1 °C | 142 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 210 °C | 410 °F | |
| Middle Barrel Temperature | 215 °C | 419 °F | |
| Front Barrel Temperature | 221 °C | 430 °F | |
| Nozzle Temperature | 227 °C | 441 °F | |
| Melt Temperature | 227 °C | 441 °F | |
| Drying Temperature | 104 °C | 219 °F | |
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | |
| Dew Point | -40.0 °C | -40.0 °F | |
| Injection Pressure | 69.0 - 103 MPa | 10000 - 14900 psi | |
| Hold Pressure | 35.0 - 69.0 MPa | 5080 - 10000 psi | |
| Back Pressure | 0.345 MPa | 50.0 psi | |
| Screw Speed | 30 - 80 rpm | 30 - 80 rpm |
Users viewing this material also viewed the following:
- Parker Chomerics Tecknit Teckfip™ HC FIP-C Formed in Place Conductive Elastomer
- IDI Composites 46-16 Thermoset Polyester, Molding
- Techmer ES Luriblend® PA6/6 CF20 TL15 BK 20% Carbon Filled
- Teknor Apex Sinvicomp SGH 4000 Polyvinyl Chloride, Flexible
- Dow C700-35N Polypropylene Impact Copolymer
- 3M 12028 Black 1/8" (3.2 mm) Polyurethane Foam
- ATI Allegheny Ludlum Stainless Steel Type AL 436S™ Ferric Stainless Steel
- Arlon 44566R020 0.020" (0.508 mm) Uncured Silicone Rubber with Fiberglass Substrate
- Asahi Glass Fluon® P-62XP PFA Perfluoropolymer
- Haynes 25 alloy, room temperature after 10% cold reduction, 1120°C anneal for 5 minutes
Copyright © lookpolymers.com All Rights Reserved