Loxim 830 01 HBCC Polypropylene Compound 30% Chemically Coupled, Flame Retardant
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene Copolymer , Polypropylene, Flame Retardant |
| Manufacturer | Loxim Industries |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Loxim 830 01 HBCC Polypropylene Compound 30% Chemically Coupled, Flame Retardant.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Loxim Industries
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.05 - 1.15 g/cc | 1.05 - 1.15 g/cc | ASTM D792 |
| Filler Content | 30 % | 30 % | |
| Linear Mold Shrinkage | 0.0040 - 0.0060 cm/cm | 0.0040 - 0.0060 in/in | ASTM D1299 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 90.0 - 100 MPa | 13100 - 14500 psi | ASTM D683 |
| Elongation at Break | 4.0 - 6.0 % | 4.0 - 6.0 % | ASTM D638 |
| Flexural Modulus | 5.00 - 5.50 GPa | 725 - 798 ksi | ASTM D790 |
| Izod Impact, Notched | 1.00 - 1.20 J/cm | 1.87 - 2.25 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 145 - 155 °C | 293 - 311 °F | ASTM D1525, HDT Method B |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
Users viewing this material also viewed the following:
- PolyOne Geon™ Vinyl Flexible XV3860 Polyvinyl Chloride, Flexible (PVC, Flexible)
- Polykemi AB POLYabs N00 ABS
- Mitsubishi Hostaphan® RN, 12 micron Nominal Thickness Universal Polyethylene Terephthalate Film
- Grupo Repol Dinalon® B1S25 G25 H PA6 25% Glass Fiber, Heat Stabilized
- Haynes 188 alloy, 30% cold reduction, 3.2 mm thick sheet, 1175°C for 5 minutes
- Techmer ES HiFill® PA6/6 GF25 L BK 25% Glass Filled
- UBE UBEPOL BR150 Non-Oil Extended Synthetic Rubber Vulcanizate (Cured 50 Minutes at 145°C)
- Clariant Renol PCSP0013WT-192 Polycarbonate, Flame Retardant, UV Stabilized, High Opacity
- Carlson C 800H Nickel-Iron-Chromium Alloy
- ExxonMobil Exceed™ 3527PA Metallocene Polyethylene Resin (European Grade)
Copyright © lookpolymers.com All Rights Reserved