- Loxim 820 02T V0 Polypropylene Compound, 20% Talc Filled, Flame Retardant
Loxim 820 02T V0 Polypropylene Compound, 20% Talc Filled, Flame Retardant
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 20% Talc Filler |
| Manufacturer | Loxim Industries |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Loxim 820 02T V0 Polypropylene Compound, 20% Talc Filled, Flame Retardant.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Loxim Industries
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.05 - 1.15 g/cc | 1.05 - 1.15 g/cc | ASTM D792 |
| Filler Content | 20 % | 20 % | |
| Linear Mold Shrinkage | 0.010 - 0.012 cm/cm | 0.010 - 0.012 in/in | ASTM D1299 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 24.0 - 26.0 MPa | 3480 - 3770 psi | ASTM D683 |
| Flexural Modulus | 2.50 - 2.70 GPa | 363 - 392 ksi | ASTM D790 |
| Izod Impact, Notched | 0.350 - 0.450 J/cm | 0.656 - 0.843 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 105 - 110 °C | 221 - 230 °F | ASTM D1525, HDT Method B |
| Flammability, UL94 | V-0 @Thickness 1.60 mm |
V-0 @Thickness 0.0630 in |
Users viewing this material also viewed the following:
- Nihon Superior SN100C Lead-Free Solder Alloy
- Industrial Laminates/Norplex NP159 Synthetic Fabric (discontinued **)
- Lehmann & Voss LUVOCOM® 80-8387/EM Polyacetal-copolymer, unreinforced
- Haynes Hastelloy® S alloy, flat products, solution heat-treated at 760°C (1400°F), aged 8000 hours
- Wico Plast Wicotal 500 Acetal
- DuPont Performance Polymers Rynite® 530 NC010 Polyethylene Terephthalate (PET) (Unverified Data**)
- Barlog Plastics KEBAFLEX E 65.1 TPE-V, Shore A65
- Ineos H07G-00 Polypropylene Homopolymer
- ExxonMobil Santoprene® 8211-60 Thermoplastic Elastomer (discontinued **)
Copyright © lookpolymers.com All Rights Reserved