- Lord Adhesives Versilok® 253 / 254 Acrylic Adhesive
Lord Adhesives Versilok® 253 / 254 Acrylic Adhesive
| Category | Polymer , Adhesive |
| Manufacturer | Lord Adhesives |
| Trade Name | Versilok® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lord Adhesives Versilok® 253 / 254 Acrylic Adhesive.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LORD Versilok® 253/254 adhesive is a two-component, epoxy-modified acrylic adhesive used to bond a variety of automotive sheet metals, including hot-dip galvanized, electro-galvanized, bare aluminum, and cold rolled steel. Versilok 253/254 adhesive can be either room temperature cured or heat cured for faster processing.Glass beads are included in the adhesive system providing a mechanical lock between substrates. Versilok 253/254 adhesive is approved by General Motors Corporation (3639M) and Ford Motor Company (ESB-M2G347-A).All information provided by Lord.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.14 - 1.25 g/cc | 0.0412 - 0.0452 lb/in³ | 253 Resin |
| 1.39 - 1.46 g/cc | 0.0502 - 0.0527 lb/in³ | 254 Hardener | |
| Brookfield Viscosity | 40000 - 300000 cP @Temperature 25.0 °C |
40000 - 300000 cP @Temperature 77.0 °F |
254 Hardener; HAT-TD @ 5rpm |
| 160000 - 520000 cP @Temperature 25.0 °C |
160000 - 520000 cP @Temperature 77.0 °F |
253 Resin; HAT-TD @ 5rpm |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Elongation at Yield | 25 - 30 % | 25 - 30 % | ASTM D638 |
| Impact Test | >= 10.2 J | >= 7.50 ft-lb | GM 9751P |
| Peel Strength | >= 5.26 kN/m | >= 30.0 pli | ASTM D1876 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Flash Point | >= 93.0 °C | >= 199 °F | 253 Resin; Closed Cup |
| >= 93.0 °C | >= 199 °F | 254 Hardener; Closed Cup |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Cure Time | 30.0 - 40.0 min @Temperature 25.0 °C |
0.500 - 0.667 hour @Temperature 77.0 °F |
Handling strength |
| Shelf Life | 6.00 Month @Temperature 25.0 °C |
6.00 Month @Temperature 77.0 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Appearance | Gray | 254 Hardener |
| White/Light Green | 253 Resin | |
| Consistency | Paste | 253 Resin |
| Paste | 254 Hardener | |
| Press Flow (sec) | 15-55 | 20g, 80psi @ 25ºC; orifice #1, 0.052" |
| 20-60 | 20g, 80psi @ 25ºC; orifice #1, 0.052" |
Users viewing this material also viewed the following:
- Advanced Elastomer Systems Santoprene® 453-45 Thermoplastic Rubber (discontinued **)
- Phillips Sumika Marlex® AGM-110 Reactor Thermoplastic Polyolefins, Cold Temperature Impact Resistant (discont
- Materion Beryllium Copper Alloy 165 Plate & Rolled Bar; HT (TH04) Temper; up to 9.5 mm Thickness (UNS C17000)
- Borealis Daplen™ KSR4525 Polypropylene Reactor Elastomer Modified
- A. Schulman INVISION™ VX-5065UI Soft Touch Polyolefin Thermoplastic
- Total PS CPDS 818R Flame Retardant Polystyrene
- A. Schulman POLYFORT™ FPP 1200H High Flow, Calcium Carbonate Fortified Homopolymer Polypropylene
- BASF Ultrason® E 3010 MR UN PESU
- Overview of materials for Polypropylene, Film Grade
- Plaslok 308 Black (INJ) Mineral/Flock Filled Phenolic Molding Compound (discontinued **)
Copyright © lookpolymers.com All Rights Reserved