Lord Adhesives Thermosetâ„¢ UR-322 Two Component Urethane Potting Compound
| Category | Polymer , Adhesive , Thermoset , Polyurethane, TS , Thermoset Polyurethane, Adhesive |
| Manufacturer | Lord Adhesives |
| Trade Name | Thermoset™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lord Adhesives Thermosetâ„¢ UR-322 Two Component Urethane Potting Compound.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Lord UR-322 is a two component, room temperature curing urethane potting compound. The cured elastomer is soft, flexible and has a very low modulus at temperatures down to -80°C. Cured UR-322 also has excellent thermal shock resistance, electrical properties and adhesion to a variety of materials. The hydrophobic nature of this resin system imparts exceptional hydrolytic stability to the cured resin.All information provided by Lord.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.950 g/cc | 0.950 g/cc | STM 2 |
| Water Absorption | 0.30 % @Temperature 25.0 °C, Time 605000 sec |
0.30 % @Temperature 77.0 °F, Time 168 hour |
ASTM D570 |
| Loss On Ignition | 0.050 % @Temperature 100 °C, Time 86400 sec |
0.050 % @Temperature 212 °F, Time 24.0 hour |
|
| Viscosity | 750 cP @Temperature 25.0 °C |
750 cP @Temperature 77.0 °F |
Mixed; STM 1 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 12 | 12 | ASTM D2240 |
| Tensile Strength, Yield | 0.689 MPa | 100 psi | ASTM D638 |
| Elongation at Yield | >= 250 % | >= 250 % | ASTM D638 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 130 °C | 266 °F | |
| Glass Transition Temp, Tg | -72.0 °C | -97.6 °F | ASTM D3418 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 5.00e+13 ohm-cm @Temperature 130 °C |
5.00e+13 ohm-cm @Temperature 266 °F |
ASTM D257 |
| 4.00e+14 ohm-cm @Temperature 105 °C |
4.00e+14 ohm-cm @Temperature 221 °F |
ASTM D257 | |
| 2.00e+16 ohm-cm @Temperature 25.0 °C |
2.00e+16 ohm-cm @Temperature 77.0 °F |
ASTM D257 | |
| Dielectric Constant | 3.1 @Frequency 1.00e+6 Hz, Temperature 25.0 °C |
3.1 @Frequency 1.00e+6 Hz, Temperature 77.0 °F |
ASTM D150 |
| Dissipation Factor | 0.20 @Frequency 1.00e+6 Hz, Temperature 25.0 °C |
0.20 @Frequency 1.00e+6 Hz, Temperature 77.0 °F |
ASTM D150 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Cure Time | 30.0 min @Temperature 25.0 °C |
0.500 hour @Temperature 77.0 °F |
Initial |
| 5760 min @Temperature 25.0 °C |
96.0 hour @Temperature 77.0 °F |
Full | |
| Pot Life | 4.0 - 5.0 min @Temperature 25.0 °C |
4.0 - 5.0 min @Temperature 77.0 °F |
|
| Shelf Life | 6.00 Month @Temperature 25.0 °C |
6.00 Month @Temperature 77.0 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Appearance | Clear | |
| Mix Ratio | 1:1 | by volume |
| 100:107 | by weight | |
| Thermal Shock | Excellent |
Users viewing this material also viewed the following:
- MV Labs CS700 CsNO3 Cesium nitrate
- Polimeri Europa Eraclene® MQ 70 U High Density Polyethylene - Injection Molding
- LG Chemical Ethylene
- Solvay SOPROPHOR® 4 D 384 Surfactant
- Covestro Apec® HT KU 1-9371 High-Heat Polycarbonate
- CIMBAR RP 9305 Talc
- Colorite Polymers 6811G-015 (Extrustion), 6812G-015 (Molding) Radiation Sterilizable Vinyl Compound
- Ametek P409L/409CB P/M Stainless Steel, Sintered from 6.45 g/cc Green Density
- Orion Engineered Carbons CORAX® HP 160 HP Carbon Black
- Plaskolite West Optix® CA - 900 High Impact Acrylic Resin
Copyright © lookpolymers.com All Rights Reserved