Lord Adhesives Aeroglaze® 9741 Epoxy Primer/Tie-Coat
| Category | Polymer , Thermoset , Epoxy |
| Manufacturer | Lord Adhesives |
| Trade Name | Aeroglaze® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lord Adhesives Aeroglaze® 9741 Epoxy Primer/Tie-Coat.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Aeroglaze® 9741 is a two-part epoxy primer designed for use on aluminum, metal, and prepared composite surfaces. Aeroglaze 9741 primer/tie-coat is applied to scuff-sanded urethane top coats and epoxy primers. It is also used as a tie coat between scuff-sanded weather worn coatings and new urethane topcoats.All information provided by Lord.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.910 g/cc | 0.0329 lb/in³ | 9700B |
| 1.34 g/cc | 0.0484 lb/in³ | Mixed | |
| 1.48 g/cc | 0.0535 lb/in³ | 9741A | |
| Solids Content | 59.6 % | 59.6 % | 9741A, by volume; ASTM D3278-82 |
| 64.1 % | 64.1 % | Mixed, by volume; ASTM D3278-82 | |
| 76 % | 76 % | 9741A, by weight; ASTM D3278-82 | |
| 76.8 % | 76.8 % | Mixed, by weight; ASTM D3278-82 | |
| 77.8 % | 77.8 % | 9700B, by volume; ASTM D3278-82 | |
| 80.3 % | 80.3 % | 9700B, by weight; ASTM D3278-82 | |
| Volatile Organic Compounds (VOC) Content | 180 g/l | 180 g/l | 9700B; ASTM D3960-89 |
| 310 g/l | 310 g/l | Mixed; ASTM D3960-89 | |
| 354 g/l | 354 g/l | 9741A; ASTM D3960-89 | |
| Viscosity Measurement | <= 30 @Temperature 25.0 °C |
<= 30 @Temperature 77.0 °F |
9741A; #4 Ford Cup (seconds); ASTM D1200 |
| <= 40 @Temperature 25.0 °C |
<= 40 @Temperature 77.0 °F |
Mixed; #4 Ford Cup (seconds); ASTM D1200 | |
| 61 @Temperature 25.0 °C |
61 @Temperature 77.0 °F |
9700B; #4 Ford Cup (seconds); ASTM D1200 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Flash Point | >= 21.7 °C | >= 71.1 °F | 9741A; Setaflash, Closed Cup; ASTM D3278-82 |
| >= 26.3 °C | >= 79.3 °F | 9700B; Setaflash, Closed Cup; ASTM D3278-82 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Cure Time | >= 300 min @Temperature 25.0 °C |
>= 5.00 hour @Temperature 77.0 °F |
|
| Pot Life | 240 min @Temperature 25.0 °C |
240 min @Temperature 77.0 °F |
|
| Shelf Life | 6.00 Month @Temperature 21.0 - 27.0 °C |
6.00 Month @Temperature 69.8 - 80.6 °F |
9741A |
| 6.00 Month @Temperature 21.0 - 27.0 °C |
6.00 Month @Temperature 69.8 - 80.6 °F |
9700B |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Appearance | Clear Amber | 9700B |
| Gray | Mixed | |
| Gray | 9741A | |
| Coating Film Dry Weight (gm/ft²/mil) | 3.77 | |
| Theoretical Coverage (ft²/gallon/mil) | 1030 |
Users viewing this material also viewed the following:
- Ravago Manufacturing Americas Enviramid™ N2300HL BK/UV2 Post Consumer Recycle Nylon 6
- PTS Tristar® PC-10FR-(V8) 8 MFI Flame Retardant, UV Stabilized Polycarbonate With Release
- Flint Hills AP5520-HA Polypropylene Impact Copolymer
- Kraton® G1657 + PA-6,6 blend (16/4/80)
- Ineos R01A-01 Polypropylene Copolymer, Antistatic
- Sax Polymers SAXAMID 226K6 Nylon 6.6, 30% Glass Beads
- Solvay Specialty Polymers Amodel® A-8950 HS Polyphthalamide (PPA), 50% Glass Fiber
- Zylog Neoplast® 180 HOFR Thermoplastic Vulcanizate
- Covestro Baydur® STR/C-410 IMR Polyurethane Composite SRIM Foam, 60% Glass Filled, MDI-based 2-Component Liquid System
- Polymer Resources PPX-SF1 Modified PPO, Structural Foam Grade, Easy Flow (Unverified Data**)
Copyright © lookpolymers.com All Rights Reserved