Toyobo GLAMIDE® T-779 Nylon-6
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 40% Mineral Filled |
| Manufacturer | Toyobo |
| Trade Name | GLAMIDE® |
| Port | Shanghai port,China |
| Trade Terms | EXW, FOB, CFR, CIF |
| Payment Terms | L/C, T/T, PayPal |
| Download PDF | Toyobo GLAMIDE® T-779 Nylon-6.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
GLAMIDE® is very tough and exhibits high abrasion resistance. It has a high melting point and heat resistance, has well-balanced proportions of mechanical properties, performs self-distinguishing and a specific grade approved as UL94V-0 class is provided, and it exhibits excellent chemical resistance and oil resistance. Grade T-779 is a mineral-reinforced Nylon-6 with high impact resistance. It is used for plating.37
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.43 g/cc | 1.43 g/cc | Absolute Drying; ASTM-D792 |
| Filler Content | 37 % | 37 % | |
| Water Absorption | 0.70 % | 0.70 % | Absolute Drying; ASTM-D570 |
| Linear Mold Shrinkage | 0.0030 - 0.0050 cm/cm <br>@Thickness 1.00 mm |
0.0030 - 0.0050 in/in <br>@Thickness 0.0394 in |
Absolute Drying |
| 0.0080 - 0.013 cm/cm <br>@Thickness 3.00 mm |
0.0080 - 0.013 in/in <br>@Thickness 0.118 in |
Absolute Drying | |
| Melt Flow | 10 g/10 min | 10 g/10 min |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 120 | 120 | Absolute Drying; ASTM-D785 |
| Tensile Strength, Ultimate | 25.0 MPa <br>@Temperature 80.0 °C |
3630 psi <br>@Temperature 176 °F |
Practical Use; ASTM-D638 |
| 31.0 MPa <br>@Temperature 80.0 °C |
4500 psi <br>@Temperature 176 °F |
Absolute Drying; ASTM-D638 | |
| 35.0 MPa <br>@Temperature 23.0 °C |
5080 psi <br>@Temperature 73.4 °F |
Practical Use; ASTM-D638 | |
| 65.0 MPa <br>@Temperature 23.0 °C |
9430 psi <br>@Temperature 73.4 °F |
Absolute Drying; ASTM-D638 | |
| 75.0 MPa <br>@Temperature -40.0 °C |
10900 psi <br>@Temperature -40.0 °F |
Practical Use; ASTM-D638 | |
| 80.0 MPa <br>@Temperature -40.0 °C |
11600 psi <br>@Temperature -40.0 °F |
Absolute Drying; ASTM-D638 | |
| Elongation at Break | 16 % | 16 % | Absolute Drying; ASTM-D638 |
| 35 % | 35 % | Practical Use; ASTM-D638 | |
| Flexural Strength | 32.0 MPa <br>@Temperature 80.0 °C |
4640 psi <br>@Temperature 176 °F |
Practical Use; ASTM-D790 |
| 48.0 MPa <br>@Temperature 80.0 °C |
6960 psi <br>@Temperature 176 °F |
Absolute Drying; ASTM-D790 | |
| 62.0 MPa <br>@Temperature 23.0 °C |
8990 psi <br>@Temperature 73.4 °F |
Practical Use; ASTM-D790 | |
| 110 MPa <br>@Temperature 23.0 °C |
16000 psi <br>@Temperature 73.4 °F |
Absolute Drying; ASTM-D790 | |
| 132 MPa <br>@Temperature -40.0 °C |
19100 psi <br>@Temperature -40.0 °F |
Practical Use; ASTM-D790 | |
| 140 MPa <br>@Temperature -40.0 °C |
20300 psi <br>@Temperature -40.0 °F |
Absolute Drying; ASTM-D790 | |
| Flexural Modulus | 0.700 GPa <br>@Temperature 80.0 °C |
102 ksi <br>@Temperature 176 °F |
Practical Use; ASTM-D790 |
| 1.10 GPa <br>@Temperature 80.0 °C |
160 ksi <br>@Temperature 176 °F |
Absolute Drying; ASTM-D790 | |
| 1.50 GPa <br>@Temperature 23.0 °C |
218 ksi <br>@Temperature 73.4 °F |
Practical Use; ASTM-D790 | |
| 4.00 GPa <br>@Temperature 23.0 °C |
580 ksi <br>@Temperature 73.4 °F |
Absolute Drying; ASTM-D790 | |
| 5.10 GPa <br>@Temperature -40.0 °C |
740 ksi <br>@Temperature -40.0 °F |
Practical Use; ASTM-D790 | |
| 5.90 GPa <br>@Temperature -40.0 °C |
856 ksi <br>@Temperature -40.0 °F |
Absolute Drying; ASTM-D790 | |
| Izod Impact, Notched | 0.600 J/cm <br>@Temperature -40.0 °C |
1.12 ft-lb/in <br>@Temperature -40.0 °F |
Absolute Drying; ASTM-D256 |
| 0.820 J/cm <br>@Temperature -40.0 °C |
1.54 ft-lb/in <br>@Temperature -40.0 °F |
Practical Use; ASTM-D256 | |
| 1.05 J/cm <br>@Temperature 23.0 °C |
1.97 ft-lb/in <br>@Temperature 73.4 °F |
Absolute Drying; ASTM-D256 | |
| NB <br>@Temperature 23.0 °C |
NB <br>@Temperature 73.4 °F |
Practical Use; ASTM-D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 74.0 µm/m-°C | 41.1 µin/in-°F | Absolute Drying; ASTM-D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 183 °C | 361 °F | Absolute Drying; ASTM-D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 96.0 °C | 205 °F | Absolute Drying; ASTM-D648 |
| Flammability, UL94 | HB | HB |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+9 ohm-cm | 1.00e+9 ohm-cm | Practical Use; ASTM-D257 |
| 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | Absolute Drying; ASTM-D257 | |
| Dielectric Strength | 16.0 kV/mm <br>@Thickness 2.00 mm |
406 kV/in <br>@Thickness 0.0787 in |
2mmt, Practical Use; ASTM-D149 |
| 21.0 kV/mm <br>@Thickness 2.00 mm |
533 kV/in <br>@Thickness 0.0787 in |
Absolute Drying; ASTM-D149 | |
| Arc Resistance | 120 sec | 120 sec | Practical Use; ASTM-D495 |
| 130 sec | 130 sec | Absolute Drying; ASTM-D495 | |
| Comparative Tracking Index | >= 600 V | >= 600 V | IEC Method |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 260 - 280 °C | 500 - 536 °F | |
| Mold Temperature | 70.0 - 110 °C | 158 - 230 °F | |
| Injection Pressure | 50.0 - 60.0 MPa | 7250 - 8700 psi |
Users viewing this material also viewed the following:
- Eastman 9921P PET Film (discontinued **)
- Inhance Fluoro-Seal INHANCE® UH-1500 Ultra High Molecular Weight Polyethylene
- Tra-Con Tra-Bond 2119 Low Viscosity Glass Laminating Adhesive
- TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane with 3.0 PHR MBT
- Fainplast Compounds GSK 78/3 Flexible PVC, Electrical Plugs Lead Free
- Arkema Group LOTRYL® 15 MA 03 Copolymer Ethylene - Methyl Acrylate
- 3M Scotchcal™ ElectroCut™ 7125-24 Graphic Film
- PolyOne Syncure™ S1060A Polyethylene, Crosslinked (XLPE)
- Master Bond Supreme 46HT-2ND2 Two Component, Non-Drip, Toughened, Epoxy Adhesive
Copyright © lookpolymers.com All Rights Reserved