Lehmann & Voss LUVOCOM® 6-8159 Polyamide 12, with carbon fiber
| Category | Polymer , Thermoplastic , Nylon , Nylon 12 , Nylon 12, Carbon Fiber Filled |
| Manufacturer | Lehmann & Voss & Co. |
| Trade Name | LUVOCOM® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lehmann & Voss LUVOCOM® 6-8159 Polyamide 12, with carbon fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Strong, stiff parts.Especially suitable at dynamic stress situations.Electrically conductive, suitable for continuous discharging of statically generated electricity.Low waterabsorbtion, for dimensional stable precision parts.Bearings, sleeves, sliding elements, chair rollers, handles.Information provided by Lehmann & Voss & Co.KG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.06 g/cc | 1.06 g/cc | ISO 1183 |
| Water Absorption | <= 0.10 % | <= 0.10 % | 23°C/24h |
| Linear Mold Shrinkage | 0.0020 - 0.0060 cm/cm | 0.0020 - 0.0060 in/in | |
| Melt Flow | 6.0 g/10 min @Load 1.20 kg, Temperature 190 °C |
6.0 g/10 min @Load 2.65 lb, Temperature 374 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Stress | 100 MPa | 14500 psi | |
| Elongation at Yield | 4.0 % | 4.0 % | |
| 6.0 % | 6.0 % | flexural | |
| Modulus of Elasticity | 6.00 GPa | 870 ksi | |
| Flexural Strength | 140 MPa | 20300 psi | |
| Flexural Modulus | 5.00 GPa | 725 ksi | |
| Charpy Impact Unnotched | 4.20 J/cm² | 20.0 ft-lb/in² | edgewise; ISO 179 1eU |
| Charpy Impact, Notched | 1.20 J/cm² | 5.71 ft-lb/in² | ISO 179 1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 90.0 °C | 194 °F | |
| 140 °C | 284 °F | short term |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | <= 1e+05 | <= 1e+05 | |
| Insulation Resistance | <= 100000 ohm | <= 100000 ohm |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 250 °C | 482 °F | mass temp |
| Nozzle Temperature | 250 - 260 °C | 482 - 500 °F | |
| Zone 1 | 230 - 250 °C | 446 - 482 °F | |
| Zone 2 | 240 - 260 °C | 464 - 500 °F | |
| Zone 3 | 250 - 270 °C | 482 - 518 °F | |
| Mold Temperature | 70.0 - 110 °C | 158 - 230 °F | |
| Drying Temperature | 75.0 °C @Time 21600 - 36000 sec |
167 °F @Time 6.00 - 10.0 hour |
Dehumidifying dryer |
| 105 °C @Time <=14400 sec |
221 °F @Time <=4.00 hour |
or |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | natural color (black) |
Users viewing this material also viewed the following:
- PolyOne Geon™ Vinyl Packaging 2710 TRN 9470 Polyvinyl Chloride, Rigid (PVC, Rigid)
- Covestro Texin® 5286 Thermoplastic Polyurethane, Polyether-based, Medical (discontinued **)
- Overview of materials for Nylon 66/6, 10% Glass Fiber Reinforced
- Huntsman IROGRAN® A 85 P 5004 TPU-Polyether
- LG Chemical LUTENE FB3000 LDPE Extrusion of Blown Film
- SABIC Innovative Plastics NORYL TN300 PPE+PS
- Westlake Elevate™ EF526 16% Ethylene Vinyl Acetate Copolymer
- Fainplast Compounds MPH 83/T Medical Flexible PVC, Extrusion
- Ashley Polymers Ashlene® 79MGS Nylon 6, 40% Glass Mineral reinforced
- Resinlab® EP1112 Black Electronic Grade Epoxy Encapsulant
Copyright © lookpolymers.com All Rights Reserved