Lehmann & Voss LUVOCOM® 6-7595 Polyamide 12, with carbon fiber
| Category | Polymer , Thermoplastic , Nylon , Nylon 12 , Nylon 12, Carbon Fiber Filled |
| Manufacturer | Lehmann & Voss & Co. |
| Trade Name | LUVOCOM® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lehmann & Voss LUVOCOM® 6-7595 Polyamide 12, with carbon fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.High-strength and high-stiff parts; low coefficient of expansion.Especially suitable at dynamic stress situations.Electrically conductive, suitable for continuous discharging of statically generated electricity.High dimensionally stable precision parts.Bearings, sleeves, sliding elements, chair rollers, handles.Information provided by Lehmann & Voss & Co.KG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.28 g/cc | 1.28 g/cc | ISO 1183 |
| Water Absorption | <= 0.10 % | <= 0.10 % | 23°C/24h |
| Linear Mold Shrinkage | 0.0020 - 0.0050 cm/cm | 0.0020 - 0.0050 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Stress | 165 MPa | 23900 psi | |
| Elongation at Yield | 2.5 % | 2.5 % | |
| 3.2 % | 3.2 % | flexural | |
| Modulus of Elasticity | 23.0 GPa | 3340 ksi | |
| Flexural Strength | 235 MPa | 34100 psi | |
| Flexural Modulus | 20.0 GPa | 2900 ksi | |
| Charpy Impact Unnotched | 3.50 J/cm² | 16.7 ft-lb/in² | flatwise; ISO 179 1fU |
| Charpy Impact, Notched | 1.10 J/cm² | 5.23 ft-lb/in² | ISO 179 1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 30.0 µm/m-°C | 16.7 µin/in-°F | DIN 53752 |
| Thermal Conductivity | 0.450 W/m-K | 3.12 BTU-in/hr-ft²-°F | DIN 52612 |
| Maximum Service Temperature, Air | 90.0 °C | 194 °F | |
| 140 °C | 284 °F | short term | |
| Vicat Softening Point | 170 °C | 338 °F | DIN ISO 306 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | <= 100 ohm | <= 100 ohm | |
| Insulation Resistance | <= 1000 ohm | <= 1000 ohm |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 250 °C | 482 °F | mass temp |
| Nozzle Temperature | 250 - 260 °C | 482 - 500 °F | |
| Zone 1 | 230 - 250 °C | 446 - 482 °F | |
| Zone 2 | 240 - 260 °C | 464 - 500 °F | |
| Zone 3 | 250 - 270 °C | 482 - 518 °F | |
| Mold Temperature | 70.0 - 110 °C | 158 - 230 °F | |
| Drying Temperature | 75.0 °C @Time 21600 - 36000 sec |
167 °F @Time 6.00 - 10.0 hour |
Dehumidifying dryer |
| 105 °C @Time <=14400 sec |
221 °F @Time <=4.00 hour |
or |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | natural color (black) |
Users viewing this material also viewed the following:
- RheTech Products FRP257-00 32% Talc Reinforced Polypropylene Copolymer, Flame Retardant, Natural
- Parker Chomerics CHO-BOND 4669 Conductive Caulk/Sealant
- PolyOne Synprene® RT-3750 Styrene Butadiene Block Copolymer (SBC) with Mineral Filler (discontinued **)
- IRPC Polimaxx Polene HI830 Polystyrene
- Teknor Apex APEX® 585 Polyvinyl Chloride, Flexible
- Wellman Wellamid® MRT1487 BK 32% Mineral Reinforced, Toughened Grade Nylon 66
- Teknor Apex Telcar® TL-2545A Thermoplastic Elastomer
- Abatron AboCoat 8501-2/AboCure 8501-2 Clear Epoxy Coating
- BASF Ultramid® A3HG7 BK 00564 35% Glass Filled PA66 (Conditioned)
- Trelleborg Emerson & Cuming Stycast® XT-1169 Two-Component Epoxy High Service Temp Encapsulant
Copyright © lookpolymers.com All Rights Reserved