Lehmann & Voss LUVOCOM® 50-8479/BL Polycarbonate, unreinforced
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | Lehmann & Voss & Co. |
| Trade Name | LUVOCOM® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lehmann & Voss LUVOCOM® 50-8479/BL Polycarbonate, unreinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Data processing machinery, precision engineering, film and photo industry, sporting and leisure goods, medical enineering.Isotropic shrinkage characteristics.Reduced moment of inertia compared with metal parts.High dimensionally stable precision parts.Handles, levers, rollers, body parts.Information provided by Lehmann & Voss & Co.KG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.37 g/cc | 1.37 g/cc | ISO 1183 |
| Water Absorption | <= 0.20 % | <= 0.20 % | 23°C/24h |
| Linear Mold Shrinkage | 0.0050 - 0.0080 cm/cm | 0.0050 - 0.0080 in/in | |
| Melt Flow | 27.4 g/10 min @Load 1.20 kg, Temperature 300 °C |
27.4 g/10 min @Load 2.65 lb, Temperature 572 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Stress | 60.0 MPa | 8700 psi | |
| Elongation at Yield | 5.0 % | 5.0 % | |
| 6.5 % | 6.5 % | flexural | |
| Modulus of Elasticity | 2.80 GPa | 406 ksi | |
| Flexural Strength | 90.0 MPa | 13100 psi | |
| Flexural Modulus | 2.40 GPa | 348 ksi | |
| Charpy Impact Unnotched | 11.0 J/cm² | 52.3 ft-lb/in² | flatwise; ISO 179 1fU |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 130 °C | 266 °F | |
| 150 °C | 302 °F | short term |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | >= 1.00e+12 ohm | >= 1.00e+12 ohm | |
| Insulation Resistance | >= 1.00e+12 ohm | >= 1.00e+12 ohm |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 295 °C | 563 °F | mass temp |
| Nozzle Temperature | 290 - 310 °C | 554 - 590 °F | |
| Zone 1 | 280 - 300 °C | 536 - 572 °F | |
| Zone 2 | 290 - 310 °C | 554 - 590 °F | |
| Zone 3 | 300 - 320 °C | 572 - 608 °F | |
| Mold Temperature | 80.0 - 120 °C | 176 - 248 °F | |
| Drying Temperature | 120 °C @Time 14400 - 21600 sec |
248 °F @Time 4.00 - 6.00 hour |
Dehumidifying dryer |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | blue |
Users viewing this material also viewed the following:
- Nilit FRIANYL A63 N-SG5 Nylon 6.6 for injection molding, 5% mineral filled
- Huntsman Rexell® L2102 Injection Molding LLDPE (discontinued **)
- Kuraray HYBRAR® HD3 Thermoplastic Rubber-HDPE Blend
- Polyram BondyRam® 1001 Maleic Anhydride modified Homo-polypropylene coupling agent
- TSE Industries Millathane® 76 Millable Polyester Polyurethane Rubber, 0.0 PHR MBT
- 3M 7215SA Screen Printable Polyester Performance Label Products with Structured Adhesive
- Unipetrol MTBE
- Beijing Evergrow Resources ER-WR-20G Polypropylene Super-Fine Filter Material
- Parker Chomerics CHO-SEAL 1315 Conductive Elastomer
- Ascend Performance Materials Vydyne® M344 BLK Nylon 66, Flame Retardant, Conditioned
Copyright © lookpolymers.com All Rights Reserved