- Lehmann & Voss LUVOCOM® 21-7979 Polyamide 6/6T, with glass fiber, 8-mm-granulate
Lehmann & Voss LUVOCOM® 21-7979 Polyamide 6/6T, with glass fiber, 8-mm-granulate
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 |
| Manufacturer | Lehmann & Voss & Co. |
| Trade Name | LUVOCOM® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lehmann & Voss LUVOCOM® 21-7979 Polyamide 6/6T, with glass fiber, 8-mm-granulate.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.High-strength and high-stiff parts; low coefficient of expansion.High dimensionally stable precision parts with low warpage and narrow tolerance range.Bearings, sleeves, sliding elements, control disks, gear wheels, duty parts in switches.Information provided by Lehmann & Voss & Co.KG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.59 g/cc | 1.59 g/cc | ISO 1183 |
| Water Absorption | <= 0.80 % | <= 0.80 % | 23°C/24h |
| Linear Mold Shrinkage | 0.0010 - 0.0030 cm/cm | 0.0010 - 0.0030 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Stress | 285 MPa | 41300 psi | |
| Elongation at Yield | 2.5 % | 2.5 % | |
| 3.2 % | 3.2 % | flexural | |
| Modulus of Elasticity | 15.0 GPa | 2180 ksi | |
| Flexural Strength | 410 MPa | 59500 psi | |
| Flexural Modulus | 13.0 GPa | 1890 ksi | |
| Charpy Impact Unnotched | 7.00 J/cm² | 33.3 ft-lb/in² | flatwise; ISO 179 1fU |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 135 °C | 275 °F | |
| 160 °C | 320 °F | short term |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | >= 1.00e+12 ohm | >= 1.00e+12 ohm | |
| Insulation Resistance | >= 1.00e+12 ohm | >= 1.00e+12 ohm |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 330 °C | 626 °F | mass temp |
| Nozzle Temperature | 330 - 340 °C | 626 - 644 °F | |
| Zone 1 | 300 - 340 °C | 572 - 644 °F | |
| Zone 2 | 310 - 340 °C | 590 - 644 °F | |
| Zone 3 | 320 - 340 °C | 608 - 644 °F | |
| Mold Temperature | 90.0 - 120 °C | 194 - 248 °F | |
| Drying Temperature | 80.0 °C @Time 21600 - 57600 sec |
176 °F @Time 6.00 - 16.0 hour |
Dehumidifying dryer |
| 110 °C @Time 14400 - 21600 sec |
230 °F @Time 4.00 - 6.00 hour |
or |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | natural color (white) |
Users viewing this material also viewed the following:
- Quantum Composites QC-8700 63% Glass Fiber Reinforced Vinyl Ester SMC
- Huntsman DY 9577 Epoxy Accelerator
- Silberline Extra Sparkle Silvet® 300-10-E1
- Silon Taborex TA 1132 HD Chemically-Crosslinkable HDPE Compound
- SABIC Innovative Plastics LNP THERMOCOMP WH0200B PBT
- Sax Polymers SAXLAC 835U Acrylonitrile Butadiene Styrene
- Loctite® 3321 Light Cure Acrylic Adhesive
- UBE Tyranno Grade D Ceramic Semi-Conductive Fiber
- PolyOne Synplast™ 9P-N Di Nonyl Phthalate
- PolyOne Edgetek® MP-30GF/000 Modified PPO - 30% Glass Fiber Reinforced (discontinued **)
Copyright © lookpolymers.com All Rights Reserved