Lehmann & Voss LUVOCOM® 1700-7910 PPO, with carbon fiber
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO |
| Manufacturer | Lehmann & Voss & Co. |
| Trade Name | LUVOCOM® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lehmann & Voss LUVOCOM® 1700-7910 PPO, with carbon fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Strong, stiff parts; low thermal coefficient of expansion.Electrically conductive, suitable for continuous discharging of statically generated electricity.High dimensionally stable precision parts with low warpage and narrow tolerance range.Control disks, cams, sliding elements and other duty parts.Information provided by Lehmann & Voss & Co.KG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.24 g/cc | 1.24 g/cc | ISO 1183 |
| Water Absorption | <= 0.060 % | <= 0.060 % | 23°C/24h |
| Linear Mold Shrinkage | 0.0010 - 0.0040 cm/cm | 0.0010 - 0.0040 in/in | |
| Melt Flow | 17.36 g/10 min @Load 5.00 kg, Temperature 300 °C |
17.36 g/10 min @Load 11.0 lb, Temperature 572 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Stress | 115 MPa | 16700 psi | |
| Elongation at Yield | 1.3 % | 1.3 % | |
| 1.5 % | 1.5 % | flexural | |
| Modulus of Elasticity | 14.0 GPa | 2030 ksi | |
| Flexural Strength | 160 MPa | 23200 psi | |
| Flexural Modulus | 12.0 GPa | 1740 ksi | |
| Charpy Impact Unnotched | 1.50 J/cm² | 7.14 ft-lb/in² | flatwise; ISO 179 1fU |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 110 °C | 230 °F |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | <= 1.00e+6 ohm | <= 1.00e+6 ohm | |
| Insulation Resistance | <= 1.00e+6 ohm | <= 1.00e+6 ohm |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 280 °C | 536 °F | mass temp |
| Nozzle Temperature | 285 - 295 °C | 545 - 563 °F | |
| Zone 1 | 270 - 280 °C | 518 - 536 °F | |
| Zone 2 | 270 - 300 °C | 518 - 572 °F | |
| Zone 3 | 290 - 305 °C | 554 - 581 °F | |
| Mold Temperature | 70.0 - 120 °C | 158 - 248 °F | |
| Drying Temperature | 95.0 - 110 °C @Time <=7200 sec |
203 - 230 °F @Time <=2.00 hour |
Dehumidifying dryer |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | silver grey |
Users viewing this material also viewed the following:
- Hybrid Plastics POSS® MA0711 MethacrylDisilanolCyclopentyl-POSS®
- Fujipoly Industries Sarcon® GR-Hb Gap Filler Pad
- H.C. Starck Amperit® 526.074 Agglomerated, Sintered Tungsten Carbide-Cobalt (WC-Co) 83-17
- Lotte Chemical Titan TITANZEX® HI2000 High density polyethylene
- Covestro Desmopan® W DP 85786A Polyurethane
- ExxonMobil Enable™ 20-10HE Metallocene Polyethylene Resin
- 3M Scotch® 24 Electrical Shielding Tape
- Ashley Polymers Ashlene® 527-25G Nylon 66, 25% Glass Reinforced
Copyright © lookpolymers.com All Rights Reserved