PolyOne Geon™ HTX Ultra LA426 Black 2880 Polyvinyl Chloride Alloy (PVC Alloy)
| Category | Polymer , Thermoplastic , Vinyl (PVC) |
| Manufacturer | PolyOne Corporation |
| Trade Name | Geon™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Geon™ HTX Ultra LA426 Black 2880 Polyvinyl Chloride Alloy (PVC Alloy).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Recommend drying material for a minimum of 2 hours at 160 degrees Farenheit. Physical properties measured on LA426 Black 2880.Information provided by PolyOne
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.22 g/cc | 1.22 g/cc | ASTM D792 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 75 | 75 | 15 sec; ASTM D2240 |
| Tensile Strength, Yield | 37.7 MPa | 5470 psi | Type I, 5.1 mm/min; ASTM D638 |
| Tensile Modulus | 1.98 GPa | 287 ksi | Type I, 5.1 mm/min; ASTM D638 |
| Flexural Strength | 66.1 MPa | 9590 psi | ASTM D790 |
| Flexural Modulus | 2.06 GPa | 299 ksi | ASTM D790 |
| Izod Impact, Notched | 6.10 J/cm @Thickness 3.18 mm, Temperature 23.0 °C |
11.4 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F |
Compression Molded; ASTM D256A |
| Dart Drop Total Energy | 65.4 J/cm @Temperature 23.0 °C |
0.123 ft-lb/mil @Temperature 73.4 °F |
Procedure A, C.125; ASTM D4226 |
| >= 178 J/cm @Temperature 23.0 °C |
>= 0.333 ft-lb/mil @Temperature 73.4 °F |
Procedure B, C.125; ASTM D4226 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 86.0 µm/m-°C | 47.8 µin/in-°F | ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 90.0 °C @Thickness 3.18 mm |
194 °F @Thickness 0.125 in |
Unannealed; ASTM D648 |
| 91.1 °C @Thickness 3.18 mm |
196 °F @Thickness 0.125 in |
Annealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 83.9 °C @Thickness 3.18 mm |
183 °F @Thickness 0.125 in |
Unannealed; ASTM D648 |
| 87.2 °C @Thickness 3.18 mm |
189 °F @Thickness 0.125 in |
Annealed; ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 174 - 193 °C | 345 - 379 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Ease of Sizing | Acceptable | |
| Features | High Impact Resistance | |
| High Stiffness | ||
| Forms | Cube | |
| Pellets | ||
| Generic Material | PVC Alloy | |
| Generic Name | Polyvinyl Chloride Alloy (PVC Alloy) | |
| Processing Method | Extrusion | |
| PVC Cell Classification | 15225 | ASTM D1784 |
| 441421540000 | ASTM D4216 | |
| Regional Availability | Africa & Middle East | |
| Asia Pacific | ||
| Europe | ||
| North America | ||
| South America | ||
| Uses | Capstock | |
| Outdoor Applications | ||
| Profiles |
Users viewing this material also viewed the following:
- RheTech Products T10P100-01 10% Talc Reinforced Polypropylene, Black
- Styrolution Novodur® 650 ABS
- A. Schulman POLYBATCH™ UVK-90 UV Stabilizer Concentrate Based In Polyethylene
- Zotefoams Plastazote® MP34 Metallocene Polyethylene Foam
- Dow Corning MOLYKOTE® 3451 CHEMICAL RESISTANT BEARING GREASE
- Clariant Renol 6608G33HSL Nylon 66, 33% Glass Fiber, Impact Modified, Heat Stabilized, Lubricated
- Cheng Yu Plastic E500G10 PC/PET, 10% Glass Fiber
- Axiall 11863 Wire & Cable Flexible PVC
- Bhansali Engineering Abstron PT-45M ABS Antistatic Extrusion Grade
- PolyOne Geon™ 180 Series 180X7 Polyvinyl Chloride Homopolymer (PVC Homopolymer)
Copyright © lookpolymers.com All Rights Reserved