Lehmann & Voss LUVOCOM® 1301-7449 PPS, linear, with carbon fiber and PTFE
| Category | Polymer , Thermoplastic , Polyphenylene Sulfide (PPS) , Polyphenylene Sulfide (PPS) with 10% Carbon Fiber Filler |
| Manufacturer | Lehmann & Voss & Co. |
| Trade Name | LUVOCOM® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lehmann & Voss LUVOCOM® 1301-7449 PPS, linear, with carbon fiber and PTFE.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Automotive industry, textile-and office machinery, medical- and precision engineering.High-strength and stiff parts with low creep.Improved friction and wear behaviour. Emergency running property.Electrically conductive, suitable for continuous discharging of statically generated electricity.High continuous use and heat distortion temperature. Non flammable.Control disks, gear wheels, pump impellers, gear parts for automotive appliances, chip carrier.Information provided by Lehmann & Voss & Co.KG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.54 g/cc | 1.54 g/cc | ISO 1183 |
| Water Absorption | <= 0.10 % | <= 0.10 % | 23°C/24h |
| Linear Mold Shrinkage | 0.00050 - 0.0020 cm/cm | 0.00050 - 0.0020 in/in | |
| Melt Flow | 10 g/10 min @Load 10.0 kg, Temperature 300 °C |
10 g/10 min @Load 22.0 lb, Temperature 572 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Stress | 180 MPa | 26100 psi | |
| Elongation at Yield | 1.0 % | 1.0 % | |
| 1.3 % | 1.3 % | flexural | |
| Modulus of Elasticity | 25.0 GPa | 3630 ksi | |
| Flexural Strength | 270 MPa | 39200 psi | |
| Flexural Modulus | 22.0 GPa | 3190 ksi | |
| Charpy Impact Unnotched | 2.50 J/cm² | 11.9 ft-lb/in² | edgewise; ISO 179 1eU |
| Coefficient of Friction, Dynamic | 0.16 | 0.16 | |
| Coefficient of Friction, Static | 0.13 | 0.13 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 9.00 µm/m-°C | 5.00 µin/in-°F | DIN 53752 |
| Thermal Conductivity | 0.750 W/m-K | 5.20 BTU-in/hr-ft²-°F | DIN 52612 |
| Maximum Service Temperature, Air | 220 °C | 428 °F | |
| 240 °C | 464 °F | short term | |
| Vicat Softening Point | 240 °C | 464 °F | DIN ISO 306 |
| Flammability, UL94 | V-0 | V-0 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | <= 100 ohm | <= 100 ohm | |
| Insulation Resistance | <= 1000 ohm | <= 1000 ohm |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 330 °C | 626 °F | mass temp |
| Nozzle Temperature | 320 - 340 °C | 608 - 644 °F | |
| Zone 1 | 300 - 320 °C | 572 - 608 °F | |
| Zone 2 | 310 - 330 °C | 590 - 626 °F | |
| Zone 3 | 320 - 340 °C | 608 - 644 °F | |
| Mold Temperature | 150 - 180 °C | 302 - 356 °F | |
| Drying Temperature | 50.0 - 90.0 °C @Time >=14400 sec |
122 - 194 °F @Time >=4.00 hour |
|
| 100 - 140 °C @Time 7200 - 14400 sec |
212 - 284 °F @Time 2.00 - 4.00 hour |
Dehumidifying dryer |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | natural color (black) |
Users viewing this material also viewed the following:
- Polymax® Maxelast® P3870H TPE, PP Overmold or Standalone use
- NOVA Chemicals Sclair® 2906 HDPE Injection Molding Resin
- Gromax BFG50-AH00B2 Nylon 6 50% Glass Filled (Conditioned)
- Kolon KOPA® KN3321G10V0L G/F Reinforced & Flame Retardant Nylon 66
- DuPont Teijin Films Melinex® ST505 Polyester Film, 500 Gauge
- C.O.I.M. LARIPUR® LPR4525 Special Adipate Ester Polyurethane
- Alliance Polymers Viprene™ G45D-32U-BLK Thermoplastic Vulcanizate Elastomer
- ATI Allegheny Ludlum Stainless Steel Chromium-Nickel Type 304L, 20% Cold Rolled (UNS S30403)
- Hexcel® HexForce™ 7544 Fiber Glass Fabric
Copyright © lookpolymers.com All Rights Reserved