- Lehmann & Voss LUVOCOM® 1301-7293/GN PPS, linear, with glass fiber
Lehmann & Voss LUVOCOM® 1301-7293/GN PPS, linear, with glass fiber
| Category | Polymer , Thermoplastic , Polyphenylene Sulfide (PPS) , Polyphenylene Sulfide (PPS) with 10% Glass Fiber Filler |
| Manufacturer | Lehmann & Voss & Co. |
| Trade Name | LUVOCOM® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lehmann & Voss LUVOCOM® 1301-7293/GN PPS, linear, with glass fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Automotive industry, textile-and office machinery, medical- and precision engineering.Strong, stiff parts.High continuous use and heat distortion temperature. Non flammable.High chemical resistance parts.High dimensionally stable precision parts with low warpage and narrow tolerance range.Gear parts for automotive appliances, body parts, grippers, spacers.Information provided by Lehmann & Voss & Co.KG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.91 g/cc | 1.91 g/cc | ISO 1183 |
| Water Absorption | <= 0.10 % | <= 0.10 % | 23°C/24h |
| Linear Mold Shrinkage | 0.00050 - 0.0030 cm/cm | 0.00050 - 0.0030 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Stress | 93.0 MPa | 13500 psi | |
| Elongation at Yield | 0.80 % | 0.80 % | |
| 1.0 % | 1.0 % | flexural | |
| Modulus of Elasticity | 18.0 GPa | 2610 ksi | |
| Flexural Strength | 135 MPa | 19600 psi | |
| Flexural Modulus | 15.0 GPa | 2180 ksi | |
| Charpy Impact Unnotched | 2.00 J/cm² | 9.52 ft-lb/in² | edgewise; ISO 179 1eU |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 220 °C | 428 °F | |
| 240 °C | 464 °F | short term | |
| Flammability, UL94 | V-0 | V-0 | not recognized by UL |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Insulation Resistance | >= 1.00e+12 ohm | >= 1.00e+12 ohm |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 330 °C | 626 °F | mass temp |
| Nozzle Temperature | 320 - 340 °C | 608 - 644 °F | |
| Zone 1 | 300 - 320 °C | 572 - 608 °F | |
| Zone 2 | 310 - 330 °C | 590 - 626 °F | |
| Zone 3 | 320 - 340 °C | 608 - 644 °F | |
| Mold Temperature | 150 - 180 °C | 302 - 356 °F | |
| Drying Temperature | 50.0 - 90.0 °C @Time >=14400 sec |
122 - 194 °F @Time >=4.00 hour |
|
| 100 - 140 °C @Time 7200 - 14400 sec |
212 - 284 °F @Time 2.00 - 4.00 hour |
Dehumidifying dryer |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | patina green |
Users viewing this material also viewed the following:
- Radici Radilon® S40E (dry) Nylon 6
- Okulen® 2000 PE-UHMW, OF
- Lucobit Lucolast® 7010 Ethylene Butyl Acrylate Asphalt Additive
- Huntsman AVALON® 85 AB Thermoplastic Polyurethane
- A. Schulman PP 828S-01 Polypropylene Medium Impact Molding Grade Polypropylene
- A. Schulman SCHULADUR® A GB30 30% Glass Bead Reinforced PBT
- Hexcel® HexPly® F263 Epoxy Resin, 7781 Glass Fabric
- ELM® TempFlex™ 0 to 100 Biodegradable Rail Curve Lubricant
- 3M Dyneon™ TFM™ 1600 PTFE
- Indium Corp. Indalloy 38 Bismuth Solder Alloy
Copyright © lookpolymers.com All Rights Reserved