Lehmann & Voss LUVOCOM® 1114-0717 PAEK, with carbon fiber and PTFE
| Category | Polymer , Thermoplastic , Polyketone , Polyaryletherketone (PAEK), Carbon Fiber Filled |
| Manufacturer | Lehmann & Voss & Co. |
| Trade Name | LUVOCOM® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lehmann & Voss LUVOCOM® 1114-0717 PAEK, with carbon fiber and PTFE.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.Good friction and wear behaviour especially at increased temperatures.Electrically conductive, suitable for continuous discharging of statically generated electricity.Thermic, mechanic and chemical highly stressed parts.Information provided by Lehmann & Voss & Co.KG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.51 g/cc | 1.51 g/cc | ISO 1183 |
| Water Absorption | <= 0.10 % | <= 0.10 % | 23°C/24h |
| Linear Mold Shrinkage | 0.0010 - 0.0030 cm/cm | 0.0010 - 0.0030 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Stress | 180 MPa | 26100 psi | |
| Elongation at Yield | 1.5 % | 1.5 % | |
| 2.0 % | 2.0 % | flexural | |
| Modulus of Elasticity | 17.0 GPa | 2470 ksi | |
| Flexural Strength | 240 MPa | 34800 psi | |
| Flexural Modulus | 14.0 GPa | 2030 ksi | |
| Charpy Impact Unnotched | 2.50 J/cm² | 11.9 ft-lb/in² | flatwise; ISO 179 1fU |
| 2.00 J/cm² @Temperature -30.0 °C |
9.52 ft-lb/in² @Temperature -22.0 °F |
ISO 179 | |
| Charpy Impact, Notched | 1.20 J/cm² | 5.71 ft-lb/in² | ISO 179 1eA |
| Coefficient of Friction, Dynamic | 0.19 | 0.19 | |
| Coefficient of Friction, Static | 0.17 | 0.17 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 5.00 µm/m-°C | 2.78 µin/in-°F | DIN 53752 |
| Thermal Conductivity | 0.600 W/m-K | 4.16 BTU-in/hr-ft²-°F | DIN 52612 |
| Maximum Service Temperature, Air | 255 °C | 491 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 305 °C | 581 °F | |
| Vicat Softening Point | 320 °C | 608 °F | DIN ISO 306 |
| Flammability, UL94 | V-0 | V-0 | not recognized by UL |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | <= 10000 ohm | <= 10000 ohm | |
| Insulation Resistance | <= 100000 ohm | <= 100000 ohm |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 390 °C | 734 °F | mass temp |
| Nozzle Temperature | 390 - 420 °C | 734 - 788 °F | |
| Zone 1 | 370 - 420 °C | 698 - 788 °F | |
| Zone 2 | 380 - 420 °C | 716 - 788 °F | |
| Zone 3 | 390 - 420 °C | 734 - 788 °F | |
| Mold Temperature | 160 - 230 °C | 320 - 446 °F | |
| Drying Temperature | 120 °C @Time 21600 - 36000 sec |
248 °F @Time 6.00 - 10.0 hour |
or |
| 150 °C @Time 14400 - 21600 sec |
302 °F @Time 4.00 - 6.00 hour |
Dehumidifying dryer |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | dark grey |
Users viewing this material also viewed the following:
- Potters Industries A-Series P-0040 Soda-Lime Silica Technical Quality Solid Glass Spheres
- Polymer Resources PC/ABS-FRG5 Flame Retardant PC/ABS Alloy, 5% Glass Reinforced
- Global EPP PA 6C Cast Polyamide 6
- Grupo Repol Dinalon® A1S25 G30 PA66 30% Glass Fiber
- SABIC Innovative Plastics LNP LUBRICOMP RVL36 PA 66 (Europe-Africa-Middle East)
- Elgiloy® Co-Cr-Ni Alloy, Strip, 65% Cold Reduction, Heat Treated
- Barlog Plastics KEBAFLEX SG 55 A.01 TPE-S, Shore A55, natural
- Asahi Kasei Thermylene® P-20FG-1714 20% Glass Fiber Reinforced, Medium Impact
- Alcoa KAMA 1200 Utility Clear OPS, Sheet (discontinued **)
Copyright © lookpolymers.com All Rights Reserved