ExxonMobil Escorene® LD-409 EVA for Low Voltage Insulation (discontinued **)

Category	Polymer , Thermoplastic , Ethylene Vinyl Acetate , Ethylene Vinyl Acetate Copolymer (EVA), Wire/Cable Grade
Manufacturer
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	ExxonMobil Escorene® LD-409 EVA for Low Voltage Insulation (discontinued **).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Data provided by the manufacturer, Exxon Chemical.A crosslinkable, 9.9% vinyl acetate copolymer designed for electrical applications.Applications: Designed to be blended with a suitable masterbatch to provide a crosslinkable low voltage cable insulation compound.

Physical Properties	Metric	English	Comments
Density	0.927 g/cc	0.0335 lb/in³	Exxon Method
Environmental Stress Crack Resistance	>= 1000 hour	>= 1000 hour	F50, Condition A; ASTM D1693
Melt Flow	4.1 g/10 min	4.1 g/10 min	Exxon Method

Mechanical Properties	Metric	English	Comments
Hardness, Shore D	38	38	ASTM D2240
Tensile Strength, Ultimate	11.4 MPa	1650 psi	ASTM D638
Elongation at Break	750 %	750 %	ASTM D638
Flexural Modulus	0.0830 GPa	12.0 ksi	ASTM D790

Thermal Properties	Metric	English	Comments
Melting Point	96.0 °C	205 °F	Exxon Method
Brittleness Temperature	<= -72.0 °C	<= -97.6 °F	ASTM D746

Electrical Properties	Metric	English	Comments
Dielectric Constant	2.45 @Frequency 1e+6 Hz	2.45 @Frequency 1e+6 Hz	ASTM D150
Dielectric Strength	18.3 kV/mm @Thickness 3.17 mm	465 kV/in @Thickness 0.125 in	ASTM D149
Dissipation Factor	0.0080 @Frequency 1e+6 Hz	0.0080 @Frequency 1e+6 Hz	ASTM D150