- HOME
- POLYMER SEARCH
- Thermoplastic
- Polyketone
- Polyetheretherketone (PEEK)
- Polyetheretherketone, PEEK, Glass Fiber Filled
- Lehmann & Voss LUVOCOM® 1105-7128 PEEK, with glass fiber, low-warpage
Lehmann & Voss LUVOCOM® 1105-7128 PEEK, with glass fiber, low-warpage
| Category | Polymer , Thermoplastic , Polyketone , Polyetheretherketone (PEEK) , Polyetheretherketone, PEEK, Glass Fiber Filled |
| Manufacturer | Lehmann & Voss & Co. |
| Trade Name | LUVOCOM® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lehmann & Voss LUVOCOM® 1105-7128 PEEK, with glass fiber, low-warpage.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.Chemical and hydrolysis resistance parts.Not flammable.High continuos use temperature.High dimensionally stable precision parts.Information provided by Lehmann & Voss & Co.KG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.51 g/cc | 1.51 g/cc | ISO 1183 |
| Water Absorption | <= 0.10 % | <= 0.10 % | 23°C/24h |
| Linear Mold Shrinkage | 0.0080 - 0.015 cm/cm | 0.0080 - 0.015 in/in | |
| Melt Flow | 19.63 g/10 min @Load 10.0 kg, Temperature 380 °C |
19.63 g/10 min @Load 22.0 lb, Temperature 716 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Stress | 88.0 MPa | 12800 psi | |
| Elongation at Yield | 2.6 % | 2.6 % | |
| 3.5 % | 3.5 % | flexural | |
| Modulus of Elasticity | 7.00 GPa | 1020 ksi | |
| Flexural Strength | 120 MPa | 17400 psi | |
| Flexural Modulus | 6.00 GPa | 870 ksi | |
| Charpy Impact Unnotched | 4.50 J/cm² | 21.4 ft-lb/in² | flatwise; ISO 179 1fU |
| Charpy Impact, Notched | 4.00 J/cm² @Temperature -30.0 °C |
19.0 ft-lb/in² @Temperature -22.0 °F |
ISO 179 eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 30.0 µm/m-°C | 16.7 µin/in-°F | DIN 53752 |
| Thermal Conductivity | 0.400 W/m-K | 2.78 BTU-in/hr-ft²-°F | DIN 52612 |
| Maximum Service Temperature, Air | 250 °C | 482 °F | |
| 260 °C | 500 °F | short term | |
| Deflection Temperature at 1.8 MPa (264 psi) | 315 °C | 599 °F | |
| Flammability, UL94 | V-0 | V-0 | not recognized by UL |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Insulation Resistance | >= 1.00e+12 ohm | >= 1.00e+12 ohm |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 390 °C | 734 °F | mass temp |
| Nozzle Temperature | 360 - 380 °C | 680 - 716 °F | |
| Zone 1 | 360 - 370 °C | 680 - 698 °F | |
| Zone 2 | 380 - 390 °C | 716 - 734 °F | |
| Zone 3 | 390 - 400 °C | 734 - 752 °F | |
| Mold Temperature | 170 - 200 °C | 338 - 392 °F | |
| Drying Temperature | 120 °C @Time 21600 - 28800 sec |
248 °F @Time 6.00 - 8.00 hour |
or |
| 150 °C @Time 10800 - 21600 sec |
302 °F @Time 3.00 - 6.00 hour |
Dehumidifying dryer |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | natural color |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics LNP THERMOCOMP WH0450EX PBT (Asia Pacific)
- Teknor Apex Sinvicomp SHE 5200 Polyvinyl Chloride, Flexible
- Hexcel® HexForce™ 7781 Fiber Glass Fabric
- Covestro Bayflex® 110-80 Polyurethane Elastomeric RIM, MDI-based 2-Component Liquid System
- Denka REOMER G G5479 Thermoplastic Elastomer, For Extrusion
- Dymax 9-20512 Voil Coil Assembly Disk Drive Adhesive
- Styron Magnum™ 9100 MFD ABS
- DuPont Performance Polymers Rynite® 530HTE NC010 Polyethylene Terephthalate (PET) (Unverified Data**)
Copyright © lookpolymers.com All Rights Reserved