Chosun Refractories HSC-16H Dense and High-Strength Castable, Credens
| Category | Ceramic , Oxide , Aluminum Oxide |
| Manufacturer | Chosun Refractories |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | EXW, FOB, CFR, CIF |
| Payment Terms | L/C, T/T, PayPal |
| Download PDF | Chosun Refractories HSC-16H Dense and High-Strength Castable, Credens.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Chosun Refractories via Korea Institute of Ceramic Engineering and Technology (KICET).
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Modulus of Rupture | 0.017658 GPa <br>@Temperature 110 °C,<br> Time 86400 sec |
2.5611 ksi <br>@Temperature 230 °F,<br> Time 24.0 hour |
|
| 0.024525 GPa <br>@Temperature 1000 °C,<br> Time 10800 sec |
3.5571 ksi <br>@Temperature 1830 °F,<br> Time 3.00 hour |
||
| 0.026487 GPa <br>@Temperature 1500 °C,<br> Time 10800 sec |
3.8417 ksi <br>@Temperature 2730 °F,<br> Time 3.00 hour |
||
| Compressive Strength | 78.5 MPa <br>@Temperature 110 °C,<br> Time 86400 sec |
11400 psi <br>@Temperature 230 °F,<br> Time 24.0 hour |
Cold Crushing Strength |
| 90.2 MPa <br>@Temperature 1000 °C,<br> Time 10800 sec |
13100 psi <br>@Temperature 1830 °F,<br> Time 3.00 hour |
Cold Crushing Strength | |
| 98.1 MPa <br>@Temperature 1500 °C,<br> Time 10800 sec |
14200 psi <br>@Temperature 2730 °F,<br> Time 3.00 hour |
Cold Crushing Strength |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 1600 °C | 2910 °F | limited |
| Shrinkage | -0.0300 % <br>@Temperature 110 °C,<br> Time 86400 sec |
-0.0300 % <br>@Temperature 230 °F,<br> Time 24.0 hour |
|
| 0.50 % <br>@Temperature 1500 °C,<br> Time 10800 sec |
0.50 % <br>@Temperature 2730 °F,<br> Time 3.00 hour |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Al2O3 | 57 % | 57 % | |
| CaO | 2.0 % | 2.0 % | |
| SiO2 | 38 % | 38 % |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Cure Time | 120 - 600 min | 2.00 - 10.0 hour | Setting Time |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Installation Method | Vibrating, Casting | |
| Material Required for Estimating(kg/?) | 2,700 | |
| Water Required for Casting(%) | 6 |
Users viewing this material also viewed the following:
- Precision Polymer Engineering E70H Ethylene Propylene Rubber
- LTL Color Compounds ColorRxâ„¢ PP2-1002ARX Biocompatible, Antimicrobial Polypropylene Random Copolymer
- Lucite International Elvacite ® 3008 Acrylic Resin
- LATI Latamid 6 H2 G/30-V0HF1 PA 6, 30% Glass Fiber Reinforced, Heat Stabilized, Flame Retardant
- Kennametal Stellite Stellite® SF12 Cobalt Alloy
- Westlake MC3033 High Density Polyethylene Coating
- A. Schulman POLYFORT™ FPP 2661 Injection Molding Grade Mineral Fortified Polypropylene
- Arlon R34066X015 0.015" (0.381 mm) Cured Silicone with Fiberglass Substrate
- Overview of materials for Linear Low Density Polyethylene (LLDPE), Compounding Resin
- Arlon 44406X015 0.015" (0.381 mm) Platinum Cured Silicone/Peroxide Catalyzed Silicone
Copyright © lookpolymers.com All Rights Reserved