- Lehmann & Voss LUVOCOM® 1100-8325 Polyether sulfone, with glass fiber and PTFE
Lehmann & Voss LUVOCOM® 1100-8325 Polyether sulfone, with glass fiber and PTFE
| Category | Polymer , Thermoplastic , Polyethersulfone (PES) , Polyethersulfone (PES), 10%Glass Fiber Filled |
| Manufacturer | Lehmann & Voss & Co. |
| Trade Name | LUVOCOM® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lehmann & Voss LUVOCOM® 1100-8325 Polyether sulfone, with glass fiber and PTFE.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Apparatus- and precision engineering, film- and photo industry, sporting- and leisure goods, medical- and electrical enineering, aircraft- and aerospace industry.Improved friction and wear behaviour. Emergency running property.High dimensionally stable precision parts, even at elevated temperatures and narrow tolerance range.Especially suitable for medical parts, superheated steam sterilizable, hydrolysis resistanceHigh quality terminal bar, switches and plugs, relais, lamp reflectors, sterilizable medical equipment.Information provided by Lehmann & Voss & Co.KG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.70 g/cc | 1.70 g/cc | ISO 1183 |
| Water Absorption | <= 0.10 % | <= 0.10 % | 23°C/24h |
| Linear Mold Shrinkage | 0.0015 - 0.0040 cm/cm | 0.0015 - 0.0040 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Stress | 120 MPa | 17400 psi | |
| Elongation at Yield | 1.6 % | 1.6 % | |
| 2.0 % | 2.0 % | flexural | |
| Modulus of Elasticity | 10.0 GPa | 1450 ksi | |
| Flexural Strength | 170 MPa | 24700 psi | |
| Flexural Modulus | 8.50 GPa | 1230 ksi | |
| Charpy Impact Unnotched | 3.00 J/cm² | 14.3 ft-lb/in² | edgewise; ISO 179 1eU |
| Coefficient of Friction, Dynamic | 0.20 | 0.20 | |
| Coefficient of Friction, Static | 0.15 | 0.15 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 180 °C | 356 °F | |
| 200 °C | 392 °F | short term | |
| Deflection Temperature at 1.8 MPa (264 psi) | 210 °C | 410 °F | |
| Vicat Softening Point | 220 °C | 428 °F | DIN ISO 306 |
| Flammability, UL94 | V-0 | V-0 | not recognized by UL |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | >= 1.00e+12 ohm | >= 1.00e+12 ohm | |
| Insulation Resistance | >= 1.00e+12 ohm | >= 1.00e+12 ohm |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 350 °C | 662 °F | mass temp |
| Nozzle Temperature | 340 - 360 °C | 644 - 680 °F | |
| Zone 1 | 355 - 375 °C | 671 - 707 °F | |
| Zone 2 | 360 - 380 °C | 680 - 716 °F | |
| Zone 3 | 350 - 370 °C | 662 - 698 °F | |
| Mold Temperature | 120 - 200 °C | 248 - 392 °F | |
| Drying Temperature | 150 °C @Time 10800 - 18000 sec |
302 °F @Time 3.00 - 5.00 hour |
Dehumidifying dryer |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | natural color (beige) |
Users viewing this material also viewed the following:
- Pyrotek Firefly 800 Roller & Furnace Cladding Material
- Polimeri Europa SINKRAL B733/E ABS, Impact & Heat Stabilized Grade (discontinued **)
- PolyOne Geon™ Vinyl Flexible R252AE Polyvinyl Chloride + NBR (PVC+NBR)
- TSE Industries Millathane® E34 Millable Polyether Polyurethane Rubber with 3.0 PHR MBT
- Ensinger Tecapeek® XP-105 Compression Molded PEEK Compound, 15% Graphite Filled
- 3M AC-275 Class B-2 Aerospace Sealant
- 3M Scotch-Weld™ RT80 Retaining Compound Anaerobic Adhesives
- PolyOne Edgetek® AM-30GM/15TF Polyphthalamide (PPA), Glass Filled, PTFE Lubricated (discontinued **)
- LATI Latamid 66 H2 G/25-V0KB4 PA 66, 25% Glass Fiber Reinforced, Heat Stabilized, Flame Retardant
Copyright © lookpolymers.com All Rights Reserved