Lehmann & Voss LUVOCOM® 1-0889-4 Polyamide 66, with carbon fiber and glass fiber, heat stabilized
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Glass/Carbon Fiber Filled |
| Manufacturer | Lehmann & Voss & Co. |
| Trade Name | LUVOCOM® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lehmann & Voss LUVOCOM® 1-0889-4 Polyamide 66, with carbon fiber and glass fiber, heat stabilized.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Strong, stiff parts.Electrically conductive, suitable for continuous discharging of statically generated electricity.Reduced moment of inertia compared with metal parts.Information provided by Lehmann & Voss & Co.KG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.32 g/cc | 1.32 g/cc | ISO 1183 |
| Water Absorption | <= 1.0 % | <= 1.0 % | 23°C/24h |
| Linear Mold Shrinkage | 0.0020 - 0.0050 cm/cm | 0.0020 - 0.0050 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Stress | 200 MPa | 29000 psi | |
| Elongation at Yield | 3.0 % | 3.0 % | |
| 3.9 % | 3.9 % | flexural | |
| Modulus of Elasticity | 12.5 GPa | 1810 ksi | |
| Flexural Strength | 290 MPa | 42100 psi | |
| Flexural Modulus | 10.5 GPa | 1520 ksi | |
| Charpy Impact Unnotched | 6.50 J/cm² | 30.9 ft-lb/in² | edgewise; ISO 179 1eU |
| Charpy Impact, Notched | 1.10 J/cm² | 5.23 ft-lb/in² | ISO 179 1eA |
| Coefficient of Friction, Dynamic | 0.31 | 0.31 | |
| Coefficient of Friction, Static | 0.27 | 0.27 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 120 °C | 248 °F | |
| 160 °C | 320 °F | short term | |
| Deflection Temperature at 1.8 MPa (264 psi) | 245 °C | 473 °F | |
| Flammability, UL94 | HB | HB | not recognized by UL |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | <= 10000 ohm | <= 10000 ohm | |
| Insulation Resistance | <= 10000 ohm | <= 10000 ohm |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 290 °C | 554 °F | mass temp |
| Nozzle Temperature | 280 - 300 °C | 536 - 572 °F | |
| Zone 1 | 290 - 310 °C | 554 - 590 °F | |
| Zone 2 | 290 - 310 °C | 554 - 590 °F | |
| Zone 3 | 290 - 310 °C | 554 - 590 °F | |
| Mold Temperature | 90.0 - 120 °C | 194 - 248 °F | |
| Drying Temperature | 75.0 °C @Time 21600 - 57600 sec |
167 °F @Time 6.00 - 16.0 hour |
Dehumidifying dryer |
| 105 °C @Time 14400 - 21600 sec |
221 °F @Time 4.00 - 6.00 hour |
Vacuum Dryer |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | black |
Users viewing this material also viewed the following:
- RheTech Products FRP102-01 Polypropylene, Flame Retardant, Black
- PolyOne OnFlex™ S KA 40A-3S1767 Thermoplastic Elastomer (TPE)
- SABIC Innovative Plastics Cycolac® MG38U ABS
- Quadrant EPP Cestilene™ HD 500 R Polyethylene
- PolyOne Geon™ Vinyl Flexible B8502 Polyvinyl Chloride, Flexible (PVC, Flexible)
- SABIC Innovative Plastics LNP Lubricomp OX95338 PPS
- SABIC Innovative Plastics Ultem HATX100 PEI+PCE (Europe-Africa-Middle East)
- Samsung Cheil Industries Starex® NH-0925U ABS, Unreinforced FR
- DuPont™ Bynel® 41E850 Anhydride Modified LLDPE
- 3M Scotchcal™ 1000-58 Graphic Film
Copyright © lookpolymers.com All Rights Reserved