- Lanxess Pocan® KU 2-7018 000000 PBT
Lanxess Pocan® KU 2-7018 000000 PBT
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), Extrusion Grade , Polybutylene Terephthalate (PBT), Impact Grade , Polybutylene Terephthalate (PBT), Unreinforced, Molded |
| Manufacturer | Lanxess |
| Trade Name | Pocan® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lanxess Pocan® KU 2-7018 000000 PBT.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PBT, non-reinforced, extrusion, injection molding, impact modified
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.24 g/cc | 0.0448 lb/in³ | ISO 1183 |
| Melt Flow | 51 g/10 min @Load 5.00 kg, Temperature 270 °C |
51 g/10 min @Load 11.0 lb, Temperature 518 °F |
Estimated using room temperature density; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 40.0 MPa | 5800 psi | ISO 527-1/-2 |
| Elongation at Break | >= 50 % | >= 50 % | Nominal; ISO 527-1/-2 |
| Elongation at Yield | 4.5 % | 4.5 % | ISO 527-1/-2 |
| Tensile Modulus | 1.75 GPa | 254 ksi | ISO 527-1/-2 |
| Charpy Impact Unnotched | NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
ISO 179/1eU |
| NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
ISO 179/1eU |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 130 µm/m-°C | 72.2 µin/in-°F | ISO 11359-1/-2 |
| CTE, linear, Transverse to Flow | 130 µm/m-°C | 72.2 µin/in-°F | ISO 11359-1/-2 |
| Melting Point | 225 °C | 437 °F | 10°C/min; ISO 11357-1/-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 90.0 °C | 194 °F | ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 50.0 °C | 122 °F | ISO 75-1/-2 |
| Vicat Softening Point | 130 °C | 266 °F | 50°C/h 50N; ISO 306 |
| Flammability, UL94 | HB @Thickness 0.800 mm |
HB @Thickness 0.0315 in |
IEC 60695-11-10 |
| HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
IEC 60695-11-10 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 250 °C | 482 °F | Injection Molding; ISO 294 |
| Mold Temperature | 80.0 °C | 176 °F | Injection Molding; ISO 10724 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Features | High impact or high impact modified | |
| Form | Pellets | |
| ISO Shortname | ISO 7792-1-PBT,GHPR,11-020 | |
| Processing | Film extrusion | |
| Injection molding | ||
| Region | Asia Pacific | |
| Europe | ||
| Near East/Africa | ||
| North America | ||
| South and Central America |
Users viewing this material also viewed the following:
- SGL Carbon Group PANOX® SM C076 SSC Oxidized Textile Fiber, Crimped staple fiber, For felts and non-wovens
- SGL Carbon Group SIGRAFIL C® C25 P250 EPY Pelletized Carbon Fiber, Epoxy Sizing
- Solvay TECHNYL® B 50 H1 PA66/6, Conditioned
- Elektro-Isola Etronax MMF Phenolic, Cotton Fabric Reinforcement, Brown, Sheets
- Eurostar Starflam BFR330A PA6, Glass Bead Reinforced, Flame Retardant, Injection Molded
- AK Steel 309S Austenitic Stainless steel
- AK Steel Cold Rolled Carbon Steel, Extra Deep Drawing Steel (EDDS), Standard Grade
- Arlon 32580X030 0.030" (0.762 mm) Uncured Unsupported Silicone Rubber on a PET Carrier
Copyright © lookpolymers.com All Rights Reserved