- HOME
- POLYMER SEARCH
- Thermoplastic
- Polyester, TP
- Polybutylene Terephthalate (PBT)
- Polybutylene Terephthalate (PBT), Unreinforced, Molded
- Lanxess Pocan® B 1100 000000 PBT
Lanxess Pocan® B 1100 000000 PBT
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), Unreinforced, Molded |
| Manufacturer | Lanxess |
| Trade Name | Pocan® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lanxess Pocan® B 1100 000000 PBT.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PBT, non-reinforced, extrusion, injection molding, improved flowability
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.30 g/cc | 0.0470 lb/in³ | ISO 1183 |
| Water Absorption | 0.50 % | 0.50 % | Test Sim. to ISO 62 |
| Moisture Absorption at Equilibrium | 0.20 % | 0.20 % | 23°C/50% R.H.; Test Sim. to ISO 62 |
| Melt Flow | 104 g/10 min @Load 2.16 kg, Temperature 250 °C |
104 g/10 min @Load 4.76 lb, Temperature 482 °F |
Estimated using room temperature density; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Modulus | 2.70 GPa | 392 ksi | ISO 527-1/-2 |
| Charpy Impact Unnotched | 9.00 J/cm² @Temperature -30.0 °C |
42.8 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU |
| 13.0 J/cm² @Temperature 23.0 °C |
61.9 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU | |
| Charpy Impact, Notched | <= 1.00 J/cm² @Temperature -30.0 °C |
<= 4.76 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA |
| <= 1.00 J/cm² @Temperature 23.0 °C |
<= 4.76 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 130 µm/m-°C | 72.2 µin/in-°F | ISO 11359-1/-2 |
| CTE, linear, Transverse to Flow | 130 µm/m-°C | 72.2 µin/in-°F | ISO 11359-1/-2 |
| Melting Point | 225 °C | 437 °F | 10°C/min; ISO 11357-1/-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 160 °C | 320 °F | ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 60.0 °C | 140 °F | ISO 75-1/-2 |
| Vicat Softening Point | 170 °C | 338 °F | 50°C/h 50N; ISO 306 |
| Flammability, UL94 | HB | HB | IEC 60695-11-10 |
| HB @Thickness 0.800 mm |
HB @Thickness 0.0315 in |
IEC 60695-11-10 | |
| Oxygen Index | 24 % | 24 % | ISO 4589-1/-2 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | IEC 60093 |
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | IEC 60093 |
| Dielectric Constant | 3.2 @Frequency 1.00e+6 Hz |
3.2 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 3.4 @Frequency 100 Hz |
3.4 @Frequency 100 Hz |
IEC 60250 | |
| Dissipation Factor | 0.0020 @Frequency 100 Hz |
0.0020 @Frequency 100 Hz |
IEC 60250 |
| 0.019 @Frequency 1.00e+6 Hz |
0.019 @Frequency 1.00e+6 Hz |
IEC 60250 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 260 °C | 500 °F | Injection Molding; ISO 294 |
| Mold Temperature | 80.0 °C | 176 °F | Injection Molding; ISO 10724 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Additives | Release agent | |
| Form | Pellets | |
| ISO Shortname | ISO 7792-1-PBT,G,07-030 | |
| Processing | Coating | |
| Film extrusion | ||
| Injection molding | ||
| Region | Asia Pacific | |
| Europe | ||
| Near East/Africa | ||
| North America | ||
| South and Central America |
Users viewing this material also viewed the following:
- Honeywell ACLAR® 33C (0.75 mil) Copolymer Film (discontinued **)
- 3M Dyneon™ TF 5065 PTFE Dispersion (discontinued **)
- KaMin Hydraprint® Kaolin Clay - Filler
- Fine Organics FINALUX GT 23 Composite Lubricant
- Saint-Gobain Tygon® Chemfluor® Convoflex™ Spiral Designed Tubing Aids in Self-flushing and Cleaning
- ChevronTexaco Heavy Duty Synthetic Automatic Transmission Fluid
- CP-Polymer-Technik Wellamid® 6600/508 HWUVCP Nylon 66, Impact Modified, UV Stabilized, Heat Stabilized, Conditioned
- ExxonMobil Mobil Pegasus 805 40
- DSM Akulon® K-FHG0 (Cond.) 50% Glass Reinforced Nylon 6 (North America) (discontinued **)
Copyright © lookpolymers.com All Rights Reserved