BASF Ultramid® A3EG3 BK00564 15% Glass Filled PA66 (Dry)
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 20% Glass Fiber Filled |
| Manufacturer | BASF |
| Trade Name | Ultramid® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | BASF Ultramid® A3EG3 BK00564 15% Glass Filled PA66 (Dry).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Ultramid A3EG3 BK00564 is a 15% glass fiber reinforced injection molding PA66 grade. It conforms to FDA requirements of 21 CFR 177.1500.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.24 g/cc | 0.0448 lb/in³ | ISO 1183 |
| Water Absorption | 7.0 % | 7.0 % | ISO 62 |
| Moisture Absorption at Equilibrium | 2.2 % | 2.2 % | 23°C/50% R.H.; ISO 62 |
| Viscosity Test | 149 cm³/g | 149 cm³/g | Viscosity number |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 122 MPa | 17700 psi | 5mm/min; ISO 527 |
| Elongation at Break | 2.5 % | 2.5 % | 5mm/min; ISO 527 |
| Izod Impact, Notched (ISO) | 5.50 kJ/m² | 2.62 ft-lb/in² | ISO Test |
| Charpy Impact, Notched | 0.550 J/cm² | 2.62 ft-lb/in² | ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 33.0 µm/m-°C | 18.3 µin/in-°F | ISO 11359 |
| CTE, linear, Transverse to Flow | 75.0 µm/m-°C | 41.7 µin/in-°F | ISO 11359 |
| Melting Point | 260 °C | 500 °F | 10 K/min |
| Deflection Temperature at 1.8 MPa (264 psi) | 246 °C | 475 °F | ISO 75 |
| Flammability, UL94 | HB @Thickness 1.66 mm |
HB @Thickness 0.0654 in |
|
| HB @Thickness 0.810 mm |
HB @Thickness 0.0319 in |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | BK00564 | |
| Commercial Status | Active America | |
| Impact Modified | No | |
| Primary Processing Technique | Injection Molding |
Users viewing this material also viewed the following:
- Nye Lubricants 723K (RL) Rheolube Grease
- Park Electrochemical Nelcote® E-761 Epoxy Prepreg, 7781 E-Glass Reinforced
- Radici Heraflex® A 80-42-90 G TPS-SEBS Thermoplastic Elastomer
- Ineos N02J-00 Polypropylene Impact Copolymer
- DSM Arnitel® EL550 Polyether Ester Elastomer (European and Asian Grade)
- Carmel Olefins CAPILENE® U 77 A Polypropylene Homopolymer
- Arkema Group EVATANE® 24-03 Copolymer Ethylene - Vinyl Acetate
- Zeon Chemicals Nipol® 9025 Polyblack Masterbatch
Copyright © lookpolymers.com All Rights Reserved