Lanxess Durethan® DP AKV 50 HR H2.0 901510 Nylon 66, 50% Glass Fiber
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 50% Glass Fiber Filled |
| Manufacturer | Lanxess |
| Trade Name | Durethan® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lanxess Durethan® DP AKV 50 HR H2.0 901510 Nylon 66, 50% Glass Fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PA 66, injection molding grade, 50% glass fibers, good heat-ageing resistance, and hydrolysis resistanceApplication Examples: coolant manifolds
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.552 g/cc | 0.05607 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.0032 cm/cm | 0.0032 in/in | ISO 294-4, 2577 |
| Linear Mold Shrinkage, Transverse | 0.0082 cm/cm | 0.0082 in/in | ISO 294-4, 2577 |
| Melt Flow | 19 g/10 min @Load 5.00 kg, Temperature 290 °C |
19 g/10 min @Load 11.0 lb, Temperature 554 °F |
Estimated using room temperature density; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 159 MPa | 23100 psi | Conditioned; ISO 527-1/-2 |
| 221 MPa | 32100 psi | ISO 527-1/-2 | |
| Elongation at Break | 2.7 % | 2.7 % | ISO 527-1/-2 |
| 4.4 % | 4.4 % | Conditioned; ISO 527-1/-2 | |
| Tensile Modulus | 10.6 GPa | 1540 ksi | Conditioned; ISO 527-1/-2 |
| 15.5 GPa | 2250 ksi | ISO 527-1/-2 | |
| Charpy Impact Unnotched | 9.50 J/cm² @Temperature 23.0 °C |
45.2 ft-lb/in² @Temperature 73.4 °F |
Conditioned; ISO 179/1eU |
| 10.0 J/cm² @Temperature -30.0 °C |
47.6 ft-lb/in² @Temperature -22.0 °F |
Conditioned; ISO 179/1eU | |
| 10.5 J/cm² @Temperature -30.0 °C |
50.0 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU | |
| 10.5 J/cm² @Temperature 23.0 °C |
50.0 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU | |
| Charpy Impact, Notched | 1.20 J/cm² @Temperature -30.0 °C |
5.71 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA |
| 1.30 J/cm² @Temperature -30.0 °C |
6.19 ft-lb/in² @Temperature -22.0 °F |
Conditioned; ISO 179/1eA | |
| 1.50 J/cm² @Temperature 23.0 °C |
7.14 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA | |
| 2.00 J/cm² @Temperature 23.0 °C |
9.52 ft-lb/in² @Temperature 73.4 °F |
Conditioned; ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 20.0 µm/m-°C | 11.1 µin/in-°F | ISO 11359-1/-2 |
| CTE, linear, Transverse to Flow | 80.0 µm/m-°C | 44.4 µin/in-°F | ISO 11359-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | >= 240 °C | >= 464 °F | ISO 75-1/-2 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Form | Pellets | |
| Processing | Injection molding | |
| Region | Asia Pacific | |
| Europe | ||
| Near East/Africa | ||
| North America | ||
| South and Central America |
Users viewing this material also viewed the following:
- PolyOne Geon™ Vinyl Wire & Cable Y594B Polyvinyl Chloride, Flexible (PVC, Flexible)
- ExxonMobil Vyram™ 9111-35W222 Thermoplastic Elastomer (discontinued **)
- Fibre Glast 3101 3K, 2x2 Twill Weave Prepreg Carbon Fiber Fabric
- Lord Adhesives Aeroglaze® 9924V Wash Primer
- Lucite International Diakon® CRG800 Acrylic Polymer, Toughened Compound
- Solvay SUPRAGIL® RM/210 EI Polynaphthalenmethan-Sulphonate, Sodium Salt
- Lubrizol Telene 1650 A/BK Dicyclopentadiene (DCPD)
- A. Schulman PP 1248-01 Polypropylene High-Flow Homopolymer Polypropylene
- Diamond Polymers ABS TM 35
- 3M Dyneon™ FC 2145 Fluoroelastomer
Copyright © lookpolymers.com All Rights Reserved