LTL Color Compounds ColorFast® PCGF120 Polycarbonate, 20% Glass-Filled
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, 20% Glass Filled |
| Manufacturer | LTL Color Compounds |
| Trade Name | ColorFast® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LTL Color Compounds ColorFast® PCGF120 Polycarbonate, 20% Glass-Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
20% glass-filled grade, good balance of impact and mechanical propertiesAll information provided by LTL Color Compounders, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.35 g/cc | 1.35 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0010 - 0.0030 cm/cm | 0.0010 - 0.0030 in/in | 0.125; ASTM D955 |
| Melt Flow | 7.0 g/10 min @Load 1.20 kg, Temperature 300 °C |
7.0 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 91 | 91 | ASTM D785 |
| Tensile Strength, Yield | 79.3 MPa | 11500 psi | 2.0 in/min; ASTM D638 |
| Elongation at Break | 5.0 % | 5.0 % | 2.0 in/min; ASTM D638 |
| Flexural Strength | 131 MPa | 19000 psi | 2.0 in/min; ASTM D790 |
| Flexural Modulus | 5.52 GPa | 800 ksi | 2.0 in/min; ASTM D790 |
| Izod Impact, Notched | 1.07 J/cm @Temperature 22.8 °C |
2.00 ft-lb/in @Temperature 73.0 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 146 °C | 295 °F | Unannealed (0.250"); ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 293 - 316 °C | 560 - 600 °F | |
| Middle Barrel Temperature | 304 - 327 °C | 580 - 620 °F | |
| Front Barrel Temperature | 316 - 338 °C | 600 - 640 °F | |
| Nozzle Temperature | 310 - 332 °C | 590 - 630 °F | |
| Melt Temperature | 316 - 338 °C | 600 - 640 °F | |
| Mold Temperature | 82.2 - 116 °C | 180 - 240 °F | |
| Drying Temperature | 121 °C | 250 °F | |
| Dry Time | 3 - 4 hour | 3 - 4 hour | nominal; maximum drying time of 48 hours |
| Back Pressure | 0.345 - 0.689 MPa | 50.0 - 100 psi | |
| Shot Size | 40 - 60 % | 40 - 60 % | |
| Vent Depth | 0.00254 - 0.00762 cm | 0.00100 - 0.00300 in | |
| Screw Speed | 40 - 70 rpm | 40 - 70 rpm |
Users viewing this material also viewed the following:
- Polymax® Maxelast® D6855 TPE, Extruded
- Polymer Resources NY66-G13-[color]H Nylon, 13% Glass Reinforced, Heat Stabilized (DAM)
- Global GP-110 High Impact Polystyrene
- Hannam Chemical Hanalac 775 ABS, Extrusion Grade
- SCG Chemicals EL-Leneâ„¢ H6670B High Density Polyethylene Film
- Eagle Brass 302 Austenitic Stainless Steel, Annealed
- ExxonMobil LD 516.LN Molding, Extrusion and Compounding Resin
- Resinlab® UR1049 MDI Based Rigid Polyurethane Foam System
Copyright © lookpolymers.com All Rights Reserved