LNP Thermocomp® JF-1006 EM Polyethersulfone, Glass Fiber Reinforcement (discontinued **)

Category	Polymer , Thermoplastic , Polyethersulfone (PES)
Manufacturer
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	LNP Thermocomp® JF-1006 EM Polyethersulfone, Glass Fiber Reinforcement (discontinued **).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Features: Good MoldabilityForms: PelletsProcessing Method: Injection MoldingInformation provided by LNP, a GE Plastics Company.This data sheet is labeled Discontinued; however many LNP grades are still active under new names instituted after the SABIC purchase.

Physical Properties	Metric	English	Comments
Specific Gravity	1.59 g/cc	1.59 g/cc	Method A; ASTM D792
Linear Mold Shrinkage	0.0030 cm/cm	0.0030 in/in	ASTM D955
Linear Mold Shrinkage, Transverse	0.0070 cm/cm	0.0070 in/in	ASTM D955

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	137 MPa	19900 psi	ASTM D638
Elongation at Break	2.6 %	2.6 %	ASTM D638
Flexural Strength	186 MPa	27000 psi	ASTM D790
Flexural Modulus	8.76 GPa	1270 ksi	ASTM D790
Izod Impact, Notched	0.587 J/cm @Thickness 3.18 mm	1.10 ft-lb/in @Thickness 0.125 in	ASTM D256
Izod Impact, Unnotched	5.34 J/cm @Thickness 3.18 mm	10.0 ft-lb/in @Thickness 0.125 in	ASTM D256

Thermal Properties	Metric	English	Comments
Deflection Temperature at 1.8 MPa (264 psi)	216 °C	421 °F	Unannealed; ASTM D648

Processing Properties	Metric	English	Comments
Melt Temperature	354 - 371 °C	669 - 700 °F
Mold Temperature	135 - 149 °C	275 - 300 °F
Drying Temperature	121 - 149 °C	250 - 300 °F
Dry Time	4 hour	4 hour
Moisture Content	0.050 %	0.050 %	Suggested
Back Pressure	0.345 - 0.689 MPa	50.0 - 99.9 psi

Users viewing this material also viewed the following: