LG Chemical TR300 MABS, Flame Retardant, Transparency

Category Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Transparent, Molded
Manufacturer LG Chemical
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LG Chemical TR300 MABS, Flame Retardant, Transparency.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Feature: Injection Molding, Flame Retardant, TransparencyApplication: Electric/Electronic Applications (TV, Monitor Housing) IT/OA deviceCAS No. 9010-94-0 and 25713-60-4Information provided by LG Chemical
Physical Properties Metric English Comments
Specific Gravity 1.05 g/cc
1.05 g/cc
ASTM D792
Water Absorption 0.50 - 1.0 %

@Temperature 23.0 °C,
Time 86400 sec
 0.50 - 1.0 %

@Temperature 73.4 °F,
Time 24.0 hour
 ASTM D570
Linear Mold Shrinkage, Flow 0.0040 - 0.0070 cm/cm

@Thickness 3.20 mm
 0.0040 - 0.0070 in/in

@Thickness 0.126 in
 ASTM D955
Melt Flow 35 g/10 min

@Load 10.0 kg,
Temperature 220 °C
 35 g/10 min

@Load 22.0 lb,
Temperature 428 °F
 ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell R 108
108
ASTM D785
Tensile Strength, Yield 42.2 MPa

@Thickness 3.20 mm
 6120 psi

@Thickness 0.126 in
 50 mm/min; ASTM D638
Elongation at Break 30 %

@Thickness 3.20 mm
 30 %

@Thickness 0.126 in
 50 mm/min; ASTM D638
Elongation at Yield >= 5.0 %

@Thickness 3.20 mm
 >= 5.0 %

@Thickness 0.126 in
 50 mm/min; ASTM D638
Tensile Modulus 2.06 GPa

@Thickness 3.20 mm
 299 ksi

@Thickness 0.126 in
 1 mm/min; ASTM D638
Flexural Yield Strength 68.6 MPa

@Thickness 6.40 mm
 9960 psi

@Thickness 0.252 in
 15 mm/min; ASTM D790
Flexural Modulus 2.16 GPa

@Thickness 6.40 mm
 313 ksi

@Thickness 0.252 in
 15 mm/min; ASTM D790
Izod Impact, Notched 0.981 J/cm

@Thickness 6.40 mm,
Temperature 23.0 °C
 1.84 ft-lb/in

@Thickness 0.252 in,
Temperature 73.4 °F
 ASTM D256
1.08 J/cm

@Thickness 3.20 mm,
Temperature 23.0 °C
 2.02 ft-lb/in

@Thickness 0.126 in,
Temperature 73.4 °F
 ASTM D256
Izod Impact, Unnotched 0.392 J/cm

@Thickness 6.40 mm,
Temperature -30.0 °C
 0.735 ft-lb/in

@Thickness 0.252 in,
Temperature -22.0 °F
 ASTM D256
0.392 J/cm

@Thickness 3.20 mm,
Temperature -30.0 °C
 0.735 ft-lb/in

@Thickness 0.126 in,
Temperature -22.0 °F
 ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 90.0 °C

@Thickness 6.40 mm
 194 °F

@Thickness 0.252 in
 Unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 82.0 °C

@Thickness 6.40 mm
 180 °F

@Thickness 0.252 in
 Unannealed; ASTM D648
Vicat Softening Point 90.0 °C

@Load 5.00 kg
 194 °F

@Load 11.0 lb
 50°C/h; ASTM D1525
UL RTI, Electrical 50.0 °C

@Thickness >=1.50 mm
 122 °F

@Thickness >=0.0591 in
 UL 746B
UL RTI, Mechanical with Impact 50.0 °C

@Thickness >=1.50 mm
 122 °F

@Thickness >=0.0591 in
 UL 746B
UL RTI, Mechanical without Impact 50.0 °C

@Thickness >=1.50 mm
 122 °F

@Thickness >=0.0591 in
 UL 746B
Flammability, UL94 V-2

@Thickness >=1.50 mm
 V-2

@Thickness >=0.0591 in