LG Chemical Lupox® PBT-HI1002F Impact Modified, Flame Retardant PBT Alloy
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) |
| Manufacturer | LG Chemical |
| Trade Name | Lupox® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LG Chemical Lupox® PBT-HI1002F Impact Modified, Flame Retardant PBT Alloy.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by US distributor Polymer Technology and Services, LLC (PTS).
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.34 g/cc | 0.0484 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0080 - 0.013 cm/cm @Thickness 1.00 - 2.50 mm |
0.0080 - 0.013 in/in @Thickness 0.0394 - 0.0984 in |
ASTM D955 |
| 0.010 - 0.015 cm/cm @Thickness 2.50 - 5.00 mm |
0.010 - 0.015 in/in @Thickness 0.0984 - 0.197 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 50.3 MPa | 7300 psi | ASTM D638 |
| Elongation at Break | 25 % @Thickness 3.17 mm |
25 % @Thickness 0.125 in |
ASTM D638 |
| Flexural Strength | 70.3 MPa @Thickness 3.17 mm |
10200 psi @Thickness 0.125 in |
ASTM D790 |
| Flexural Modulus | 1.86 GPa @Thickness 3.17 mm |
270 ksi @Thickness 0.125 in |
ASTM D790 |
| Izod Impact, Notched | 1.87 J/cm @Thickness 6.35 mm |
3.50 ft-lb/in @Thickness 0.250 in |
ASTM D256 |
| 4.27 J/cm @Thickness 3.17 mm |
8.00 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 97.8 °C | 208 °F | ASTM D648 |
| Flammability, UL94 | 5VA | 5VA | V-0/0.090" |
| V-0 @Thickness 0.762 mm |
V-0 @Thickness 0.0300 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 240 - 260 °C | 464 - 500 °F | |
| Middle Barrel Temperature | 250 - 270 °C | 482 - 518 °F | |
| Front Barrel Temperature | 250 - 270 °C | 482 - 518 °F | |
| Nozzle Temperature | 260 - 280 °C | 500 - 536 °F | |
| Melt Temperature | 260 - 280 °C | 500 - 536 °F | |
| Mold Temperature | 40.0 - 80.0 °C | 104 - 176 °F | Surface |
| Drying Temperature | 120 °C | 248 °F | 5 hr. |
| 140 °C | 284 °F | 3 hr. | |
| 120 °C @Time 18000 sec |
248 °F @Time 5.00 hour |
||
| 140 °C @Time 10800 sec |
284 °F @Time 3.00 hour |
||
| Injection Pressure | 41.4 - 62.1 MPa | 6000 - 9000 psi | Second |
| 48.3 - 75.8 MPa | 7000 - 11000 psi | First | |
| Back Pressure | 0.000 - 0.345 MPa | 0.000 - 50.0 psi | |
| Shot Size | 40 - 80 % | 40 - 80 % | |
| Vent Depth | 0.00254 - 0.00381 cm | 0.00100 - 0.00150 in |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Ram Speed Setting | Medium to Fast | |
| Screw Speed | Medium |
Users viewing this material also viewed the following:
- MV Labs RH400 RhCl3·xH2O Rhodium(III) chloride hydrate
- Lehmann & Voss LUVOCOM® 80-7752 Polyacetal-copolymer, with carbon fiber and PTFE
- Meilian Chemical PE305A RED MASTERBATCH
- Ineos ABS TRIAX® 1120 ABS/Nylon Blend, Injection Grade, Dry as Molded
- Gromax BTE30-DN00N1 Nylon 6 (Dry)
- Tra-Con Tra-Bond 2248 High Temperature Epoxy Staking Adhesive
- Covestro Bayflex® 110-50 Polyurethane Elastomeric RIM, 15% Mineral Filled, MDI-based 2-Component Liquid System
- Braskem TI60035NB High Impact Copolymer Polypropylene
- Aremco Corr-Paint™ CP2010 High Temperature Protective Coating Urethane, Aluminum Filled
- Overview of materials for Acrylic, Gamma Radiation Resistant, Molded
Copyright © lookpolymers.com All Rights Reserved