Ashley Polymers Ashlene® 527-25G Nylon 66, 25% Glass Reinforced
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Glass Fiber Filled |
| Manufacturer | Ashley Polymers |
| Trade Name | Ashlene® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Ashley Polymers Ashlene® 527-25G Nylon 66, 25% Glass Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
A 25% glass reinforced impact modified Nylon 66.Data provided by the manufacturer
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.28 g/cc | 0.0462 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0050 cm/cm | 0.0050 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 107 MPa | 15500 psi | ATSM D638 |
| Elongation at Break | 4.0 % | 4.0 % | ASTM D638 |
| Flexural Modulus | 5.20 GPa | 754 ksi | ASTM D790 |
| Izod Impact, Notched | 1.60 J/cm | 3.00 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 252 °C | 486 °F | ASTM D3418 |
| Deflection Temperature at 0.46 MPa (66 psi) | 218 °C | 424 °F | ASTM D648 |
Users viewing this material also viewed the following:
- Karina Micro-Ex 4648/1-EXPO Black PVC Compound
- MarkeTech Repton EXP 383 Alumina 96%
- Haynes 242® alloy
- SABIC Innovative Plastics Valox® ENH3500 PBT (Asia Pacific)
- A. Schulman POLYBATCH™ Woodland Green 30233U/4 Concentrate Based In LLDPE
- Chosun Refractories SS50 Special High-Density Gunning Castable
Copyright © lookpolymers.com All Rights Reserved